Granted Patent B2

US 9,447,262 · App. 13/038,507 · Granted Sep 20, 2016

Abstract

Claims (54)

1. A particulate-filled rubber composition comprising:

(i) at least one vulcanizable rubber;

(ii) at least one silane-reactive particulate filler;

(iii) at least one blocked mercaptosilane possessing two thioacyl groups, the blocked mercaptosilane having the formula:

[R 1 C(═O)S(CH 2 ) n -] 2 G-R 2 SiX 1 X 2 X 3 ; and,

(iv) at least one blocked mercaptosilane possessing a single thioacyl group, the blocked mercaptosilane having the formula:

R 3 C(═O)SR 4 SiX 1 X 2 X 3 ,

wherein

R 1 is methyl;

R 2 is ethylene;

R 3 is an alkyl group containing from 5 to 9 carbon atoms and bonded to the carbonyl group through a primary carbon atom;

R 4 is propylene;

G is a trivalent cyclohexane;

X 1 is ethoxy;

X 2 is ethoxy;

X 3 is ethoxy; and,

n is an integer 2, wherein blocked mercaptosilane (iii) is from 10 to 25 weight percent based on the total weight of blocked mercaptosilanes (iii) and (iv).

2. The particulate-filled rubber composition of claim 1 wherein the at least one sulfur-vulcanizable rubber (i) is selected from the group consisting of solution styrene-butadiene rubber (sSBR), solution styrene-butadiene rubber (sSBR) having bound styrene content in a range of 5 to 50 percent, solution styrene-butadiene rubber (sSBR) having bound styrene content in a range of 9 to 36 percent, emulsion polymerized styrene-butadiene rubber (eSBR), emulsion polymerized styrene-butadiene rubber (eSBR) having a styrene content of 20 to 28 percent bound styrene, emulsion polymerized styrene-butadiene rubber (eSBR) having a styrene content of 30 to 45 percent bound styrene, styrene-butadiene rubber (SBR), natural rubber (NR), polybutadiene (BR), polybutadiene (BR)containing 90 weight percent cis-1,4-content, ethylene-propylene co- and ter- polymers (EP, EPDM), acrylonitrile-butadiene rubber (NBR), cis-1,4-polyisoprene rubber, 3,4-polyisoprene rubber, isoprene/butadiene rubber, styrene/isoprene/butadiene terpolymer rubber, cis-1,4-polybutadiene, medium vinyl polybutadiene rubber containing 35 percent to 50 percent vinyl, high vinyl polybutadiene rubber containing 50 percent to 75 percent vinyl, styrene/isoprene copolymers, emulsion polymerization prepared styrene/butadiene/acrylonitrile terpolymer rubber and butadiene/acrylonitrile copolymer rubber.

3. The particulate-filled rubber composition of claim 1 wherein silane-reactive particulate filler (ii) is selected from the group consisting of pyrogenic silica, precipitated silica, titanium dioxide, aluminosilicate, alumina, clays, talc and mixtures thereof.

4. The particulate-filled rubber composition of claim 3 wherein the total amount of silane-reactive particulate filler (ii) is from 5 to 140 phr.

5. The particulate-filled rubber composition of claim 1 wherein blocked mercaptosilane (iv) is 3-triethoxysilylpropyl thiooctanoate.

6. The particulate-filled rubber composition of claim 1 wherein the total amount of the blocked mercaptosilanes (iii) and (iv) is from 0.2 to 12 parts by weight per hundred parts by weight of rubber.

7. The particulate-filled rubber composition of claim 1 wherein blocked mercaptosilane (iii) is 4-(2-triethoxysilylethyl)-1,2-bis-(3-thia-4-oxopentyl)cyclohexane and blocked mercaptosilane (iv) is 3-triethoxysilylpropyl thiooctanoate.

8. The particulate-filled rubber composition of claim 1 further comprising at least one additional component selected from the group consisting of inert particulate filler(s), curing aid(s), activator(s), retarder(s), accelerator(s), processing additive(s), resin(s), plasticizer(s), pigment(s), fatty acid(s), zinc oxide, wax(es), antioxidant(s), antiozonant(s) and peptizing agent(s).

9. The particulate-filled rubber composition of claim 1 wherein the amount of silane-reactive filler (ii) is from 5 to 140 parts per hundred parts by weight rubber, and the total amount of blocked mercaptosilane (iii) and blocked mercaptosilane (iv) is from 0.05 to 25 parts by weight per hundred parts by weight of rubber.

10. The particulate-filled rubber composition of claim 9 wherein said particulate-filled rubber is selected from the group consisting of:

(1) particulate-filled rubber composition comprising components (i), at least part of (ii), at least part of (iii), at least part of (iv) and the remainder of (ii) pre-reacted with the remainder of (iii) and the remainder of (iv);

(2) particulate-filled rubber composition comprising components (i), at least part of (ii), at least part of (iv) and the remainder of (ii) pre-reacted with all of (iii) and the remainder of (iv);

(3) particulate-filled rubber composition comprising components (i), at least part of (ii), at least part of (iii) and the remainder of (ii) pre-reacted with the remainder of (iii) and all of (iv);

(4) particulate-filled rubber composition comprising components (i), at least part of (iii), at least part of (iv) and all of (ii) pre-reacted with the remainder of (iii) and the remainder of (iv);

(5) particulate-filled rubber composition comprising components (i), at least part of (iv) and all of (ii) pre-reacted with all of (iii) and the remainder of (iv);

(6) particulate-filled rubber composition comprising (i), at least part of (iii) and all of (ii) pre-reacted with the remainder of (iii) and all of (iv); and,

(7) particulate-filled rubber composition comprising (i) and all of (ii) pre-reacted with all of (iii) and all of (iv).

11. The vulcanized rubber composition of claim 1 .

12. The vulcanized rubber composition of claim 8 .

13. The vulcanized rubber composition of claim 9 .

14. The vulcanized rubber composition of claim 10 .

15. An article made from the particulate filled rubber composition of claim 1 .

16. The article of claim 15 which is a tire, tire component, hose, belt, roller, insulation, jacketing, industrial good, shoe sole, bushing or damping pad.

17. An article made from the particulate filled rubber composition of claim 8 .

18. The article of claim 17 which is a tire, tire component, hose, belt, roller, insulation, jacketing, industrial good, shoe sole, bushing or damping pad.

19. An article made from the particulate filled rubber composition of claim 9 .

20. The article of claim 19 which is a tire, tire component, hose, belt, roller, insulation, jacketing, industrial good, shoe sole, bushing or damping pad.

21. An article made from the particulate filled rubber composition of claim 10 .

22. The article of claim 21 which is a tire, tire component, hose, belt, roller, insulation, jacketing, industrial good, shoe sole, bushing or damping pad.

23. A free-flowing filler composition comprising the particulate-filled rubber composition of claim 1 .

24. A process for making the particulate-filled rubber composition of claim 1 comprising:

a) thermomechanically mixing, components (i), (ii), (iii) and (iv) of claim 1 at a first elevated temperature in at least one preparatory mixing step

b) blending the mixture result from (a) with at least one acyl-reactive deblocking agent and, optionally, at least one vulcanization agent, at a second elevated temperature which is below the first elevated temperature; and, optionally,

c) curing said mixture at a third elevated temperature and for a period of time sufficient to effect curing of the mixture resulting from (b).

25. The process of claim 24 , wherein blocked mercaptosilane (iii) is 4-(2-triethoxysilylethyl)-1,2-bis-(3-thia-4-oxopentyl)clohexane.

26. The process of claim 24 wherein blocked mercaptosilane (iv) is 3-triethoxysilylpropyl thiooctanoate.

27. The process of claim 24 wherein in step (a), (i) 100 parts by weight of vulcanizable rubber selected from the group consisting of conjugated diene homopolymers, conjugated diene copolymer, copolymer of at least one conjugated dime of at least one aromatic vinyl compound and mixtures thereof are mixed with (ii) from 5 to 140 parts per hundred parts by weight rubber of at least one silane-reactive particulate filler or a mixture of from 15 to 99 weight percent at least one silane-reactive particulate filler and, correspondingly, from 1 to 85 weight percent of at least one inert particulate filler and (iii) from 0.05 to 25 parts per hundred part by weight rubber in the total of blocked mercaptosilane (iii) and blocked mercaptosilane (iv).

28. The process of claim 24 wherein at least part up to the full amount of silane-reactive filler (ii), at least part up to the full amount of blocked mercaptosilane (iii) and at least part up to the full amount of blocked mercaptosilane (iv) are provided as the reaction product of silane-reactive particulate filler (ii) and mixture of blocked mercaptosilane (iii) and blocked mercaptosilane (iv).