Composite materials with blend of thermoplastic particles
View Patent ↗Pre-impregnated composite material (prepreg) is provided that can be cured to form composite parts that have high levels of damage tolerance. The matrix resin includes a thermoplastic particle component that is a blend of particles that have a melting point above the curing temperature and particles that have a melting point at or below the curing temperature.
1. A pre-impregnated composite material for curing at a curing temperature, said pre-impregnated composite material comprising:
A) reinforcing fibers; and
B) a matrix comprising:
a) a resin component comprising a difunctional epoxy resin, a trifunctional meta-glycidyl amine and a tetrafunctional para-glycidyl amine;
b) a thermoplastic particle component comprising high melting thermoplastic particles that have a melting point above said curing temperature and low melting thermoplastic particles that have a melting point at or below said curing temperature;
d) a thermoplastic toughening agent;
e) electrically conducting particles; and
f) a curing agent.
2. A pre-impregnated composite material according to claim 1 wherein said curing temperature is between 140° C. and 200° C.
3. A pre-impregnated composite material according to claim 1 wherein said high melting thermoplastic particles are selected from the group consisting of polyamide 6 and said low melting thermoplastic particles are selected from the group consisting of copolymers of polyamide 6 and polyamide 12.
4. A pre-impregnated composite material according to claim 1 wherein said reinforcing fibers are selected from the group consisting of glass, carbon and aramid.
5. A pre-impregnated composite material according to claim 1 wherein said difunctional epoxy resin is selected from the group consisting of diglycidyl ether of bisphenol F, diglycidyl ether of bisphenol A, diglycidyl dihydroxy naphthalene and combinations thereof.
6. A pre-impregnated composite material according to claim 1 wherein said electrically conductive particles comprise silver, gold, copper, aluminum, nickel, conducting grades of carbon, buckminsterfullerene, carbon nanotubes, carbon nanofibers, nickel coated carbon particles and/or silver coated copper particle.
7. A pre-impregnated composite material according to claim 6 wherein said electrically conducting particles comprise one or more conducting grades of carbon.
8. A pre-impregnated composite material according to claim 1 wherein the amount of said high melting thermoplastic particles in said thermoplastic component is about equal to the amount of said low melting thermoplastic particles in said thermoplastic component.
9. A pre-impregnated composite material according to claim 1 wherein said toughening agent is selected from the group consisting of polyether sulfone, polyether ethersulfone, polyphenyl sulphone, polysulfone, polyimide, polyetherimide, aramid, polyamide, polyester, polyketone, polyetheretherketone, polyurethane, polyurea, polyarylether, polyarylsulphide, polycarbonate and polyphenylene oxide.
10. A pre-impregnated composite material according to claim 1 wherein said curing agent is an aromatic amine.
11. A composite part that comprises a pre-impregnated composite material according to claim 1 wherein said matrix has been cured at said curing temperature.
12. A method for making a composite part comprising the step of curing a pre-impregnated composite material according to claim 1 at said curing temperature.
13. A method for making a pre-impregnated composite material for curing at a curing temperature, said method comprising the steps of:
A) providing a reinforcing fiber; and
B) impregnating said reinforcing fiber with a matrix wherein said matrix comprises:
a) a resin component comprising a difunctional epoxy resin, a trifunctional meta-glycidyl amine and a tetrafunctional para-glycidyl amine;
b) a thermoplastic particle component comprising high melting thermoplastic particles that have a melting point above said curing temperature and low melting thermoplastic particles that have a melting point at or below said curing temperature;
d) a thermoplastic toughening agent;
e) electrically conducting particles; and
f) a curing agent wherein said curing temperature is between 140° C. and 200° C.
14. A method for making a pre-impregnated composite material according to claim 13 wherein said high melting thermoplastic particles are selected from the group consisting of polyamide 6 and said low melting thermoplastic particles are selected from the group consisting of copolymers of polyamide 6 and polyamide 12.
15. A method for making a pre-impregnated composite material according to claim 13 wherein said reinforcing fibers are selected from the group consisting of glass, carbon and aramid.
16. A method for making a pre-impregnated composite material according to claim 13 wherein said difunctional epoxy resin is selected from the group consisting of diglycidyl ether of bisphenol F, diglycidyl ether of bisphenol A, diglycidyl dihydroxy naphthalene and combinations thereof.
17. A method for making a pre-impregnated composite material according to claim 13 wherein said electrically conductive particles comprise silver, gold, copper, aluminum, nickel, conducting grades of carbon, buckminsterfullerene, carbon nanotubes, carbon nanofibers, nickel coated carbon particles and/or silver coated copper particle.
18. A method for making a pre-impregnated composite material according to claim 17 wherein said electrically conducting particles comprise one or more conducting grades of carbon.
19. A method for making a pre-impregnated composite material according to claim 13 wherein the amount of said high melting thermoplastic particles in said thermoplastic component is about equal to the amount of said low melting thermoplastic particles in said thermoplastic component.
20. A method for making a pre-impregnated composite material according to claim 13 wherein said toughening agent is selected from the group consisting of polyether sulfone, polyether ethersulfone, polyphenyl sulphone, polysulfone, polyimide, polyetherimide, aramid, polyamide, polyester, polyketone, polyetheretherketone, polyurethane, polyurea, polyarylether, polyarylsulphide, polycarbonate and polyphenylene oxide.
21. A method for making a pre-impregnated composite material according to claim 13 wherein said curing agent is an aromatic amine.
22. A method according to claim 13 that comprises the additional step of curing said pre-impregnated composite material.