Heat-shrinkable polyester film
View Patent ↗A heat-shrinkable polyester film having a heat-shrinkage change per degree Celsius (%/° C.) along the main shrinkage direction of 1.5 to 3.0 in the range of 60° C. to 70° C., 2.5 to 3.5 in the range of 70° C. to 80° C., 1.0 to 2.0 in the range of 80° C. to 90° C., and 0.1 to 1.0 in the range of 90° C. to 100° C., has a good appearance quality after shrinkage and thus suitable for a wrapping material, particularly a label for a bottle.
1. A heat-shrinkable polyester film having a heat-shrinkage change per degree Celsius (%/° C.) along the main shrinkage direction of 1.5 to 3.0 in the range of 60° C. to 70° C., 2.5 to 3.5 in the range of 70° C. to 80° C., 1.0 to 2.0 in the range of 80° C. to 90° C., and 0.1 to 1.0 in the range of 90° C. to 100° C.,
wherein the heat-shrinkable polyester film is prepared by using a copolyester composition comprising:
(i) a dibasic acid component comprising at least 90 mol % of terephthalic acid residue based on 100 mol % of the dibasic acid component; and
(ii) a diol component comprising (a) 1 to 20 mol % of diethylene glycol, (b) 5 to 30 mol % of neopentyl glycol, and (c) 50 to 90 mol % of ethylene glycol, based on 100 mol % of the diol component.
2. The heat-shrinkable polyester film of claim 1 , wherein the copolyester composition further comprises at least one selected from the group consisting of a reaction catalyst, a polymer stabilizer, a reaction additive, and an inorganic material.
3. The heat-shrinkable polyester film of claim 1 , wherein the copolyester composition has an intrinsic viscosity of 0.6 to 0.9 dl/g.
4. A heat-shrinkable polyester film having a heat-shrinkage change per degree Celsius (%/° C.) along the main shrinkage direction of 1.5 to 3.0 in the range of 60° C. to 70° C., 2.5 to 3.5 in the range of 70° C. to 80° C., 1.0 to 2.0 in the range of 80° C. to 90° C., and 0.1 to 1.0 in the range of 90° C. to 100° C., which has a heat-shrinkage ratio of 58% or more along the main shrinkage direction, a skirt ratio (S/R) represented by formula (I) of 14% or less, and a maximum shrinkage stress of 6N or less, when treated in hot water at 90° C. for 10 seconds:
Skirt Ratio (%)=( W−d )/ L ×100 (I)
wherein, L is the length of the film along the main shrinkage direction, W is the width of the film before shrinkage, and d is the width of the film after shrinkage.
5. A method for preparing a heat-shrinkable polyester film having a heat-shrinkage change per degree Celsius (%/° C.) along the main shrinkage direction of 1.5 to 3.0 in the range of 60° C. to 70° C., 2.5 to 3.5 in the range of 70° C. to 80° C., 1.0 to 2.0 in the range of 80° C. to 90° C., and 0.1 to 1.0 in the range of 90° C. to 100° C., the method comprising the steps of:
(a) melt-extruding a copolyester composition to obtain a sheet and then drawing the sheet in the main shrinkage direction at a temperature ranging from Tg+5° C. to Tg+20° C. to obtain an oriented film; and
(b) heat-treating the oriented film at a temperature ranges between Tg+5° C. and Tg+50° C.
6. The method of claim 5 , wherein the copolyester composition comprises:
(i) a dibasic acid component comprising at least 90 mol % of terephthalic acid residue based on 100 mol % of the dibasic acid component; and
(ii) a diol component comprising (a) 1 to 20 mol % of diethylene glycol, (b) 5 to 30 mol % of neopentyl glycol, and (c) 50 to 90 mol % of ethylene glycol, based on 100 mol % of the diol component.