High conductive, soft urethane rollers
View Patent ↗Rollers for high speed printers and paper handling devices are fabricated by reacting polymeric diphenylmethane diisocyanate with a polyester polyol and/or polyester polyamine and an optional extender, together with a metal salt, a catalyst, and one or more other optional additives, including a liquid conductive additive. The resulting rollers provide a hardness as low as 15 A on cube, a resistivity as low as 5E4 Ω·cm, a compression set as low as 0.5% at room temperature and as low as 3% at 157° F., and low tackiness as low as 13 g/cm of adhesion force.
1. A conductive thermoset urethane formed from a mixture comprising:
a polymeric diphenylmethane diisocyanate;
a soft segment comprising a polyester polyol, a polyester polyamine, or a combination thereof;
a hard segment comprising a polyol, a polyamine, or a combination thereof; and
a metal salt,
wherein the weight ratio of the soft segment to the hard segment is at least 100, and the conductive thermoset urethane has a compression set of less than 5% at room temperature.
2. The conductive thermoset urethane of claim 1 , wherein the weight ratio of the soft segment to the hard segment is at least 200.
3. The conductive thermoset urethane of claim 1 , wherein the mixture further comprises a liquid conductive additive comprising an additional metal salt dissolved in a solvent.
4. The conductive thermoset urethane of claim 3 , wherein the additional metal salt is an alkali metal salt or a transition metal salt.
5. The conductive thermoset urethane of claim 3 , wherein the solvent is selected from the group consisting of tris(2-butoxyethyl phosphate), tri(β-chloroethyl) phosphate, and tri(β-chloropropyl) phosphate.
6. The conductive thermoset urethane of claim 1 , wherein the compression set of the conductive thermoset urethane is as low as 0.5% at room temperature or as low as 3% at 157° F.
7. The conductive thermoset urethane of claim 1 , wherein the hardness of the conductive thermoset urethane is as low as 15 Shore A on cube.
8. The conductive thermoset urethane of claim 1 , wherein the volume resistivity of the conductive thermoset urethane is as low as 5E4 Ω·cm.
9. The conductive thermoset urethane of claim 1 , wherein the soft segment has an equivalent weight of at least 900.
10. The conductive thermoset urethane of claim 1 , wherein the hard segment has an equivalent weight of less than 200.
11. The conductive thermoset urethane of claim 1 , wherein the metal salt comprises an alkali metal salt or a transition metal salt.
12. The conductive thermoset urethane of claim 1 , wherein a weight percentage of the metal salt in the conductive thermoset urethane is between 0.1 wt % and 8 wt %.
13. The conductive thermoset urethane of claim 1 , wherein the adhesion force of the conductive thermoset urethane is between 5 g/cm and 50 g/cm.
14. The conductive thermoset urethane of claim 1 , wherein the soft segment is selected from the group consisting of a polyester polyol, a polyester polyamine, or a combination thereof.
15. The conductive thermoset urethane of claim 1 , wherein the hard segment is selected from the group consisting of a polyol, a polyamine, or a combination thereof.
16. A roller for a printing or paper handling device, the roller comprising:
a cylindrical metal core; and
a conductive thermoset urethane formed around the cylindrical metal core, the conductive thermoset urethane formed from a mixture comprising:
a polymeric diphenylmethane diisocyanate;
a soft segment comprising a polyester polyol, a polyester polyamine, or a combination thereof;
a hard segment comprising a polyol, a polyamine, or a combination thereof; and
a metal salt,
wherein the weight ratio of the soft segment to the hard segment is at least 100, and the conductive thermoset urethane has a compression set of less than 5% at room temperature.
17. The roller of claim 16 , wherein roller comprises an adhesive coating between the cylindrical metal core and the conductive thermoset urethane.
18. The roller of claim 16 , further comprising a top coating applied to the surface of the conductive thermoset polyurethane.
19. The roller of claim 16 , wherein the roller is selected from the group consisting of developer rollers, charge rollers, exit rollers, toner add rollers, and bias transport rollers.