Curable silicone impression materials with high tear strength and low consistency

1. A curable material comprising:

component (A) comprising at least two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule;

component (B) comprising organohydrogenpolysiloxane with at least three SiH groups per molecule;

component (D) comprising a catalyst for promoting the reaction between (A) and (B);

component (F) comprising filler; and

component (H) comprising at least one silane with at least two alkenyl groups per molecule,

wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm.

2. The material according to claim 1 , wherein the viscosity of at least one of the organopolysiloxanes of component (A) is at least twice the viscosity of another organopolysiloxane of component (A).

3. The material according to claim 1 comprising:

5-70 wt.-% components (A), (B), and (H) combined;

0-40 wt.-% organopolysiloxane without reactive groups;

0.00005-0.05 wt.-% catalyst (D), calculated as elemental platinum and relative to the total weight of the material;

0-10 wt.-% hydrophilizing agents;

10-90 wt.-% component (F);

0-5 wt.-% conventional dental additives, adjuvants and colorants; and

0.1-50 wt.-% component (H).

4. The material according claim 3 comprising:

10-60 wt.-% components (A), (B), and (H) combined;

0-20 wt.-% organopolysiloxane without reactive groups;

0.0002-0.04 wt.-% catalyst (D), calculated as elemental platinum and relative to the overall weight of the material;

0-2 wt-% hydrophilizing agent;

30-80 wt.-% component (F);

0-2 wt.-% conventional dental additives, adjuvants and colorants; and

0.1-20 wt.-% component (H).

5. The material according claim 1 , wherein the quantities of components (A), (B) and (H) are selected such that 0.5 to 10 mol SiH units in component (B) are present per mol of unsaturated double bond in components (A) and (H).

6. The material according to claim 1 wherein, said material is prepared from two pasty compositions in the form of a base paste and a catalyst paste, wherein the entire amount of said organohydrogenpolysiloxane is present in the base paste, and the entire amount of said catalyst is present in the catalyst paste, and the remaining components are distributed between the two pastes.

7. The material according to claim 6 , wherein the volume ratio of base paste to catalyst paste in the material is 10:1 to 1:10.

8. The material according to claim 1 , wherein component A comprises at least three different types of organopolysiloxanes, each with a different viscosity and one organopolysiloxane has a higher viscosity than the other two.

9. The material according to claim 1 , wherein the curable material is a dental impression material.

10. A curable material comprising:

component (A) comprising at least two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule, with the proviso that the component (A) siloxanes do not comprise aromatic groups;

component (B) comprising organohydrogenpolysiloxane with at least three SiH groups per molecule;

component (D) comprising a catalyst for promoting the reaction between (A) and (B);

component (F) comprising filler; and

component (H) comprising at least one silane with at least two alkenyl groups per molecule,

wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm; and

wherein, upon curing, the material has a Shore A hardness of no greater than about 70.

11. The material according to claim 10 , wherein the curable material is a dental impression material.

12. A curable material comprising:

component (A) comprising at least two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule;

component (B) comprising organohydrogenpolysiloxane;

component (D) comprising a catalyst for promoting the reaction between (A) and (B);

component (F) comprising filler; and

component (H) comprising at least one silane with at least two alkenyl groups per molecule

wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm;

wherein, upon curing, the material has an elongation at break value of 70 to 300%.

13. The curable material of claim 12 , wherein, upon curing, the material has a Shore A hardness of no greater than about 70.

14. A curable material comprising:

component (A) consisting of two different types of organopolysiloxanes, (A1) having a viscosity value of 10 to 1,000 mPa-s, and (A2) having a viscosity value of 500 to 45,000 mPa-s, with at least two ethylenically unsaturated groups per molecule, with the proviso that the component (A) siloxanes do not comprise aromatic groups;

component (B) comprising organohydrogenpolysiloxane with at least three SiH groups per molecule;

component (D) comprising a catalyst for promoting the reaction between (A) and (B);

component (F) comprising filler; and

component (H) comprising at least one silane with at least two alkenyl groups per molecule; wherein said at least one silane is selected from the group consisting of compounds that can be represented by the general formula (II)

Si(R1) n (R2)4- n   (II)

wherein R1 is a linear, branched or cyclic monovalent ethylenically unsaturated substituent which can undergo an addition reaction with SiH-groups, having from 2 to 12 carbon atoms, R2 is a monovalent radical without groups that can undergo an addition reaction with SiH-groups and n is 2, 3 or 4,

wherein the consistency of the curable material according to ISO 4823 is greater than 40 mm.

15. The curable material of claim 14 , wherein, upon curing, the material has a Shore A hardness of no greater than about 70.

16. The curable material of claim 14 , wherein component A comprises at least three different types of organopolysiloxanes, each with a different viscosity and one organopolysiloxane has a higher viscosity than the other two.