Ferrite composition and electronic component
View Patent ↗A ferrite composition includes a main component having 46.0 to 49.8 mol % of an iron oxide in terms of Fe 2 O 3 , 5.0 to 14.0 mol % of a copper oxide in terms of CuO and 8.0 to 32.0 mol % of a zinc oxide in terms of ZnO, and a remainder of the main component is composed of a nickel oxide; and as subcomponents, with respect to 100 wt % of the main component, 0.5 to 6.0 wt % of a silicon oxide in terms of SiO 2 and 0.01 to 2.0 wt % of a boron oxide in terms of B 2 O 3 . Further, as a subcomponent, 0.01 to 0.17 wt % of potassium oxide in terms of K 2 O or 0.3 to 2.0 wt % of tin oxide in terms of SnO 2 may be included.
1. A ferrite composition comprising:
a main component including 46.0 to 49.8 mol % of iron oxide in terms of Fe 2 O 3 , 5.0 to 14.0 mol % of copper oxide in terms of CuO and 8.0 to 32.0 mol % of zinc oxide in terms of ZnO, and a remainder of said main component is composed of nickel oxide; and
as subcomponents, with respect to 100 wt % of said main component, 0.5 to 6.0 wt % of silicon oxide in terms of SiO 2 and 0.01 to 2.0 wt % of boron oxide in terms of B 2 O 3 .
2. The ferrite composition as set forth in claim 1 further comprising:
as a subcomponent, 0.01 to 0.17 wt % of potassium oxide in terms of K 2 O with respect to 100 wt % of said main component.
3. The ferrite composition as set forth in claim 1 further comprising:
as a subcomponent, 0.3 to 2.0 wt % of tin oxide in terms of SnO 2 with respect to 100 wt % of said main component.
4. The ferrite composition as set forth in claim 2 further comprising:
as a subcomponent, 0.3 to 2.0 wt % of tin oxide in terms of SnO 2 with respect to 100 wt % of said main component.
5. The ferrite composition as set forth in claim 1 , wherein
an average crystal particle size of a crystal particle included in said ferrite composition is 0.2 to 1.1 μm.
6. The ferrite composition as set forth in claim 2 , wherein
an average crystal particle size of a crystal particle included in said ferrite composition is 0.2 to 1.3 μm.
7. The ferrite composition as set forth in claim 3 , wherein
an average crystal particle size of a crystal particle included in said ferrite composition is 0.2 to 1.1 μm.
8. The ferrite composition as set forth in claim 4 , wherein
an average crystal particle size of a crystal particle included in said ferrite composition is 0.2 to 1.3 μm.
9. An electronic component comprising said ferrite composition as set forth in claim 1 .
10. An electronic component comprising said ferrite composition as set forth in claim 2 .
11. An electronic component comprising said ferrite composition as set forth in claim 3 .
12. An electronic component comprising said ferrite composition as set forth in claim 4 .