Method for producing difluorophosphate, nonaqueous electrolyte solution for secondary batteries, and nonaqueous electrolyte secondary battery
View Patent ↗The present invention provides a simple method for producing a difluorophosphate from a source material, the difluorophosphate being useful as additives for nonaqueous electrolyte solutions for secondary batteries. In the method, a source material containing a carbonate and/or a borate is allowed to react with a source gas which contains P and F and which may further contain O as required. The source material may contain lithium carbonate. The source gas may be produced by decomposing LiPF 6 . The source gas may be produced in such a manner that LiPF 6 and lithium carbonate are mixed and then subjected to reaction. The nonaqueous electrolyte solution contains the product obtained from the reaction.
1. A nonaqueous electrolyte solution comprising a nonaqueous solvent, a hexafluorophosphate, difluorophosphate, and fluoride dissolved therein.
2. The nonaqueous electrolyte solution according to claim 1 , wherein the difluorophosphate is produced by a method comprising bringing a source gas into contact with a source material comprising at least one component selected from the group consisting of a carbonate and a borate,
wherein the source gas comprises a phosphorus compound consisting of P and F and/or a phosphorus compound consisting of P, F, and O.
3. The nonaqueous electrolyte according to claim 2 , wherein the phosphorus compound is at least one phosphorus compound selected from the group consisting of PF 5 and POF 3 .
4. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 1 , a negative electrode, and a positive electrode.
5. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 1 , a negative electrode, and a positive electrode, wherein at least one of the following conditions is satisfied:
(i) the sum of the electrode areas of the positive electrode is 20 times or more greater than the surface area of a cover of the secondary battery;
(ii) the secondary battery has a direct current resistance of less than ten milliohms (mΩ); and
(iii) the electrical capacity of a battery cell housed in a battery cover of the secondary battery is three ampere-hours (Ah) or more.
6. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 1 , a negative electrode that conducts lithium ions, and a positive electrode.
7. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 1 , a negative electrode that conducts lithium ions, and a positive electrode, wherein at least one of the following conditions is satisfied:
(i) the sum of the electrode areas of the positive electrode is 20 times or more greater than the surface area of a cover of the secondary battery;
(ii) the secondary battery has a direct current resistance of less than ten milliohms (mΩ); and
(iii) the electrical capacity of a battery cell housed in a battery cover of the secondary battery is three ampere-hours (Ah) or more.
8. A nonaqueous electrolyte solution comprising a nonaqueous solvent, a hexafluorophosphate, difluorophosphate, and carbon dioxide dissolved therein.
9. The nonaqueous electrolyte solution according to claim 8 , wherein the difluorophosphate is produced by a method comprising bringing a source gas into contact with a source material comprising at least one component selected from the group consisting of a carbonate and a borate,
wherein the source gas comprises a phosphorus compound consisting of P and F and/or a phosphorus compound consisting of P, F, and O.
10. The nonaqueous electrolyte according to claim 9 , wherein the phosphorus compound is at least one phosphorus compound selected from the group consisting of PF 5 and POF 3 .
11. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 8 , a negative electrode, and a positive electrode.
12. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 8 , a negative electrode, and a positive electrode, wherein at least one of the following conditions is satisfied:
(i) the sum of the electrode areas of the positive electrode is 20 times or more greater than the surface area of a cover of the secondary battery;
(ii) the secondary battery has a direct current resistance of less than ten milliohms (mΩ); and
(iii) the electrical capacity of a battery cell housed in a battery cover of the secondary battery is three ampere-hours (Ah) or more.
13. The nonaqueous electrolyte solution according to claim 8 , wherein the difluorophosphate is produced by a method comprising mixing LiPF 6 with a source material comprising at least one component selected from the group consisting of a carbonate and a borate, and then heating the mixture.
14. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 8 , a negative electrode that conducts lithium ions, and a positive electrode.
15. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 8 , a negative electrode that conducts lithium ions, and a positive electrode, wherein at least one of the following conditions is satisfied:
(i) the sum of the electrode areas of the positive electrode is 20 times or more greater than the surface area of a cover of the secondary battery;
(ii) the secondary battery has a direct current resistance of less than ten milliohms (mΩ); and
(iii) the electrical capacity of a battery cell housed in a battery cover of the secondary battery is three ampere-hours (Ah) or more.
16. A nonaqueous electrolyte solution comprising a nonaqueous solvent, a hexafluorophosphate, and lithium difluorophosphate dissolved therein, wherein the nonaqueous solvent comprises a cyclic carbonate and a linear carbonate, and wherein a PO 3 F content and PO 4 content are less than or equal to one weight percent of the non-metal component weight, and wherein the nonaqueous electrolyte solution comprises at least one further component selected from the group consisting of fluoride and carbon dioxide.
17. The nonaqueous electrolyte solution according to claim 16 , wherein the cyclic carbonate is at least one carbonate selected from the group consisting of ethylene carbonate, propylene carbonate, and butylene carbonate and the linear carbonate is at least one carbonate selected from the group consisting of dimethyl carbonate, diethyl carbonate, and ethyl methyl carbonate.
18. The nonaqueous electrolyte solution according to claim 16 , wherein the nonaqueous solvent comprises ethylene carbonate, dimethyl carbonate, and diethyl carbonate.
19. The nonaqueous electrolyte solution according to claim 16 , wherein the nonaqueous solvent comprises ethylene carbonate, dimethyl carbonate, and ethyl methyl carbonate.
20. The nonaqueous electrolyte solution according to claim 1 , wherein the difluorophosphate is produced by a method comprising mixing LiPF 6 with a source material comprising at least one component selected from the group consisting of a carbonate and a borate, and then heating the mixture.
21. The nonaqueous electrolyte solution according to claim 16 , wherein the nonaqueous solvent is a solvent mixture of three or more nonaqueous solvent components.
22. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 16 , a negative electrode that conducts lithium ions, and a positive electrode.
23. A nonaqueous electrolyte secondary battery comprising the nonaqueous electrolyte solution according to claim 16 , a negative electrode that conducts lithium ions, and a positive electrode, wherein at least one of the following conditions is satisfied:
(i) the sum of the electrode areas of the positive electrode is 20 times or more greater than the surface area of a cover of the secondary battery;
(ii) the secondary battery has a direct current resistance of less than ten milliohms (mΩ); and
(iii) the electrical capacity of a battery cell housed in a battery cover of the secondary battery is three ampere-hours (Ah) or more.