Silica-based sols
View Patent ↗The present invention relates to a silica-based sol having a concentration of soluble silica of less than about 1000 mg SiO 2 /l, conductivity of at least about 2.0 mS/cm and S-value below about 50%. The invention further relates to a method of producing a silica-based sol comprising subjecting an aqueous alkali metal silicate solution to electrodialysis to form an electrodialyzed sol, and acidifying the electrodialyzed sol to form an acidified sol having a pH in the range of from about 5.0 to about 10. The invention further relates to silica-based sol obtainable by the process and to the use of the silica-based sol as a flocculating agent. The invention further relates to a process for producing paper which comprises providing an aqueous suspension comprising cellulosic fibers, adding to the suspension one or more drainage and retention aids comprising a silica-based sol according to the invention, and dewatering the obtained suspension to provide a sheet or web of paper.
1. A silica-based sol having an SiO 2 , content of at least about 3% by weight, a concentration of soluble silica of less than about 800 mg SiO 2 /l, conductivity of at least about 2.0 mS/cm and S-value below about 50%.
2. The silica-based sol according to claim 1 , wherein the concentration of soluble silica is less than about 750 mg SiO 2 /l.
3. The silica-based sol according to claim 1 , wherein the sol has a conductivity of at least about 2.5 mS/cm.
4. The silica-based sol according to claim 1 , wherein the sol has an S-value within the range of from about 8 to about 30%.
5. The silica-based sol according to claim 1 , wherein the sol contains silica-based particles having a specific surface area of at least about 300 m 2 /g.
6. The silica-based sol according to claim 1 , wherein the sol contains silica-based particles that are not modified with aluminium.
7. The silica-based sol according to claim 1 , wherein the sol has a SiO 2 content of at least about 4% by weight.
8. The silica-based sol according to claim 2 , wherein the sol has a conductivity of at least about 2.5 mS/cm.
9. The silica-based sol according to claim 3 , wherein the sol has an S-value within the range of from about 8 to about 30%.
10. The silica-based sol according to claim 8 , wherein the sol has an S-value within the range of from about 8 to about 30%.
11. The silica-based sol according to claim 4 , wherein the sol contains silica-based particles having a specific surface area of at least about 300 m 2 /g.
12. The silica-based sol according to claim 5 , wherein the sol has a SiO 2 content of at least about 4% by weight.
13. A flocculating agent comprising the silica-based sol according to claim 1 .
14. A process for producing paper comprising:
(i) providing an aqueous suspension comprising cellulosic fibres;
(ii) adding to the suspension one or more draining and retention aids comprising a silica-based sol according to claim 1 ; and
(iii) dewatering the obtained suspension to provide a sheet or web of paper.
15. The process according to claim 14 , wherein said one or more drainage and retention aids comprise a cationic starch or a cationic synthetic polymer.