View Patent ↗The present invention relates to a mixture including at least O,O-tert-butyl-O-(2-ethylhexyl) monoperoxycarbonate and at least O,O-tert-amyl-O-2-ethylhexyl monoperoxycarbonate, where the O,O-tert-amyl-O-2-ethylhexyl monoperoxycarbonate is present in the mixture in an amount of from 0.001% to 45% by weight relative to the total weight of the mixture. The invention also relates to a crosslinkable composition that includes such a peroxide mixture and an elastomer; and to uses of the crosslinkable composition and mixture.
1. A mixture comprising O,O-tert-butyl-O-(2-ethylhexyl) monoperoxycarbonate and O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate, wherein the O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate is present in the mixture in an amount of from 10% to 35% by weight relative to the total weight of the mixture.
2. The mixture of claim 1 , wherein the amount of the O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate is present in an amount of from 15% to 30% by weight relative to the total weight of the mixture.
3. The mixture of claim 1 , wherein the mixture consists of the O,O-tert-butyl-O-(2-ethylhexyl) monoperoxycarbonate and the O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate.
4. The mixture of claim 3 , wherein the amount of the O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate is present in an amount of from 10% to 35% by weight relative to the total weight of the mixture.
5. A crosslinkable composition comprising at least one ethylene vinyl acetate copolymer and the mixture of claim 1 , wherein the ethylene-vinyl acetate copolymer is present in the composition in an amount of from 85% to 99.5% by weight relative to the weight of the composition.
6. The crosslinkable composition of claim 5 , further comprising at least one antioxidant.
7. The crosslinkable composition of claim 6 , wherein the antioxidant is present in the composition in an amount of from 0.1% to 3% by weight relative to the weight of the composition.
8. A method of of increasing the rate of crosslinking comprising combining at least the mixture of claim 1 and at least one ethylene-vinyl acetate copolymer to form a crosslinkable composition, wherein the ethylene-vinyl acetate copolymer is present in the crosslinkable composition in an amount of from 85% to 99.5% by weight relative to the weight of the composition, and wherein the amount of the O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate is present in an amount of from 10% to 35% by weight relative to the total weight of the mixture.
9. A process for crosslinking comprising at least the step of reacting a composition comprising a) at least one ethylene-vinyl acetate copolymer, b) O,O-tert-butyl-O-(2-ethylhexyl) monoperoxycarbonate and c) O,O-tert-amyl-O-2-ethylhexyl monoperoxycarbonate, wherein the amount of O,O-tert-amyl-O-2-ethylhexyl monoperoxycarbonate is from 10% to 35% by weight relative to the total weight of the O,O-tert-butyl-O-(2-ethylhexyl) monoperoxycarbonate and O,O-tert-amyl-O-2-ethylhexyl monoperoxycarbonate in the composition.
10. The process of claim 9 , wherein the ethylene-vinyl acetate copolymer is present in the composition in an amount of from 85% to 99.5% by weight relative to the weight of the composition.
11. A process for manufacturing a film comprising the steps of: a) extruding into a film a crosslinkable composition comprising at least one ethylene-vinyl acetate copolymer, O,O-tert-butyl-O-(2-ethylhexyl) monoperoxycarbonate and O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate, wherein the amount of O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate is from 10% to 35% by weight relative to the total weight of the O,O-tert-butyl-O-(2-ethylhexyl) monoperoxycarbonate and O,O-tert-amyl-O-(2-ethylhexyl) monoperoxycarbonate in the composition; and b) crosslinking the composition during or after the extrusion step.