Ceramic honeycomb structure and its production method
A ceramic honeycomb structure having a large number of flow paths defined by porous cell walls having porosity of 45-68% and an average pore size of 15-35 μm, the volume of pores having diameters of more than 50 μm being more than 10% and 25% or less of the total pore volume, the volume of pores having diameters of 100 μm or more being 1-8% of the total pore volume, the volume of pores having diameters of less than 10 μm being 3-10% of the total pore volume, and the pores having a pore size distribution deviation σ [=log(D 20 )−log(D 80 )] of 0.45 or less, wherein D 20 represents a pore size (μm) at a pore volume corresponding to 20% of the total pore volume, and D 80 represents a pore size (μm) at a pore volume corresponding to 80% of the total pore volume, in a curve showing the relation between a pore size and a cumulative pore volume obtained by accumulating a pore volume from the maximum pore size to a particular pore size, and D 80 <D 20 .
1. A ceramic honeycomb structure having a large number of flow paths defined by porous cell walls having porosity of 45-68% and an average pore size of 15-35 μm, said ceramic honeycomb structure having a thermal expansion coefficient of 3 ×10 −7 /° C. to 13 ×10 −7 /° C. between 20° C. and 800° C., and pores meeting the following conditions:
the volume of pores having diameters of more than 50 μm being more than 10% and 25% or less of the total pore volume;
the volume of pores having diameters of 100 μm or more being 1-8% of the total pore volume;
the volume of pores having diameters of less than 10 μm being 3-10% of the total pore volume; and
said pores having a pore size distribution deviation σ[=log(D 20 )−log(D 80 )] of 0.45 or less, wherein D 20 represents a pore size (μm) at a pore volume corresponding to 20% of the total pore volume, and D 80 represents a pore size (μm) at a pore volume corresponding to 80% of the total pore volume, in a curve showing the relation between a pore size and a cumulative pore volume obtained by accumulating a pore volume from the maximum pore size to a particular pore size, and D 80 <D 20 .
2. The ceramic honeycomb structure according to claim 1 , wherein said porous cell walls have air permeability of 4 ×10 −12 m 2 to 9 ×10 −12 m 2 .
3. The ceramic honeycomb structure according to claim 1 , having an isostatic strength of 1 MPa or more.
4. The ceramic honeycomb structure according to claim 1 , wherein said porous cell walls have a thickness of 0.2-0.3 mm and a cell density of 23-39 cells/cm 2 .
5. The ceramic honeycomb structure according to claim 1 , which suffers pressure loss of 1.2 kPa or less, when capturing 2 g/liter of soot at a flow rate of 10 Nm 3 /min with a ceramic honeycomb filter obtained by alternately plugging flow path ends of a ceramic honeycomb structure of 266.7 mm in diameter and 304.8 mm in length having a cell density of 36.4 cells/cm 2 and a cell wall thickness of 0.28 mm in a checkerboard pattern.
6. The ceramic honeycomb structure according to claim 1 , wherein a main component of its crystal phase is cordierite, containing 3-6% of spinel and 1-8% of cristobalite.
7. The ceramic honeycomb structure according to claim 1 , wherein said porosity is more than 58% and 66% or less.
8. The ceramic honeycomb structure according to claim 1 , wherein said average pore size is 20-34 μm.
9. A method for producing a ceramic honeycomb structure having a large number of flow paths defined by porous cell walls by extrusion-molding a moldable material comprising a cordierite-forming material and a pore-forming material, and sintering the resultant molding,
said cordierite-forming material containing 10-20% of silica;
said silica being in the form of powder having a mode diameter of 30-60 μm, particles having particle sizes of 20 μm or less being 2-10%, particles having particle sizes of 100 μm or more being 2-10%, and particles having particle sizes of 200 μm or more being 1% or less;
said particles having a particle size distribution deviation SD [=log(d 80 )−log(d 20 )] of 0.5 or less, wherein d 20 represents a particle size (μm) corresponding to a cumulative volume of 20%, and d 80 represents a particle size (μm) corresponding to a cumulative volume of 80%, in a curve showing the relation between a particle size and a cumulative particle volume expressed by the volume percentage of particles having a particular particle size or less, and meeting d 20 <d 80 ; and wherein the method produces a ceramic honeycomb structure according to claim 1 .
10. The method for producing a ceramic honeycomb structure according to claim 9 , wherein said pore-forming material is 1-15% based on said cordierite-forming material, and wherein said pore-forming material is in the form of powder having a mode diameter of 30-70 μm and a particle size distribution deviation SD of 0.5 or less.
11. The method for producing a ceramic honeycomb structure according to claim 9 , wherein the absolute value of the difference between the mode diameter M50 of said silica particles and the mode diameter m50 of said pore-forming material particles, |M50-m50|, is 15 μm or less.
12. The method for producing a ceramic honeycomb structure according to claim 9 , wherein said silica particles have sphericity of 0.5 or more.
13. The method for producing a ceramic honeycomb structure according to claim 9 , wherein said pore-forming material is more than 6% and 15% or less, based on said cordierite-forming material.