Corrosion-resistant magnet and method for producing the same
View Patent ↗An object of the present invention is to provide an R—Fe—B based sintered magnet that exhibits excellent corrosion resistance and maintains excellent adhesion strength to an adherend even under severe conditions, and a method for producing the same. A corrosion-resistant magnet of the present invention as a means for achieving the object is characterized by comprising a chemical conversion film containing at least Zr, V, Al, fluorine, and oxygen as constituent elements and not containing phosphorus over a surface of an R—Fe—B based sintered magnet with a film made of Al or an alloy thereof therebetween.
1. A method for producing a corrosion-resistant magnet characterized by comprising vapor depositing a film made of Al or an alloy thereof on a surface of an R—Fe—B based sintered magnet at a first average film formation rate set at 0.1 μm/min to 0.4 μm/min until one-third of a desired film thickness is reached and then at a second average film formation rate of 0.2 μm/min to 1 μm/min, the second average film formation rate being always higher than the first average film formation rate, and then forming, on the surface of the deposited film, a chemical conversion film containing at least Zr, V, Al, fluorine, and oxygen as constituent elements and not containing phosphorus,
wherein the corrosion-resistant magnet is characterized in that a region of an outer-surface-side half of the thickness of the chemical conversion film has a higher Zr content than a region of a magnet-side half of the thickness of the chemical conversion film.