Method of preparing gel polymer electrolyte secondary battery and gel polymer electrolyte secondary battery

1. A method of preparing a gel polymer electrolyte secondary battery including a cathode, an anode, a separator and a gel polymer electrolyte in a battery case, the method comprising:

(S1) manufacturing a cathode and an anode by adding a polymerization initiator to either a cathode slurry or an anode slurry, or both of the slurries, the slurry including an electrode active material, a conductive material, a binder and a solvent, coating the resultant slurry on a current collector, and pressing the slurry onto the current collector and drying the slurry;

(S2) putting an electrode assembly including the cathode, the anode and a separator of a non-woven fabric into a battery case; and

(S3) forming a gel polymer electrolyte by introducing a gel polymer electrolyte composition including an electrolyte solvent, an electrolyte salt and a polymer electrolyte monomer into the battery case and polymerizing the monomer.

wherein the binder of (S1) is inert to chemical reactions initiated by the polymerization initiator and the slurry of (S1) do not have polymer electrolyte monomer therein.

2. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 ,

wherein the non-woven fabric separator is formed of polyethylene or polypropylene.

3. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 ,

wherein the polymerization initiator is at least one selected from the group consisting of benzoyl peroxide, acetyl peroxide, dilauryl peroxide, di-tert-butyl peroxide, t-butyl-peroxy-2-ethylhexanoate, cumyl hydroperoxide, t-amyl-(2-ethylhexyl)monoperoxy carbonate, hydrogen peroxide, 2,2′-azobis(2-cyanobutane), 2,2′-azobis(methylbutyronitrile), AIBN and AMVN.

4. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 ,

wherein the polymer electrolyte monomer is a monomer having a polymerizable functional group selected from the group consisting of a vinyl group, an epoxy group, an allyl group and a (meth)acryl group.

5. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 ,

wherein the electrolyte solvent is at least one selected from the group consisting of cyclic carbonate, linear carbonate, lactone, ether, ester, sulfoxide, acetonitrile, lactam, ketone and halogen derivatives thereof.

6. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 ,

wherein the electrolyte salt is a combination of (i) a positive ion selected from the group consisting of Li + , Na + and K + , and (ii) a negative ion selected from the group consisting of PF 6 − , BF 4 − , Cl − , Br − , I − , ClO 4 − , AsF 6 − , CH 3 CO 2 − , CF 3 SO 3 − , N(CF 3 SO 2 ) 2 − and C(CF 2 SO 2 ) 3 − .

7. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 ,

wherein the monomer is included in an amount of 0.01 to 10 parts by weight based on 100 parts by weight of a mixture of the electrolyte solvent and the electrolyte salt.

8. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 ,

wherein the polymerization initiator is included in an amount of 0.01 to 5 parts by weight based on 100 parts by weight of a mixture of the electrolyte solvent and the electrolyte salt.

9. The method of preparing a gel polymer electrolyte secondary battery according to claim 1 , further comprising:

performing thermal treatment or light radiation in the polymerization.

10. A gel polymer electrolyte secondary battery prepared according to claim 1 .

11. The gel polymer electrolyte secondary battery according to claim 10 , further comprising:

performing thermal treatment or light radiation in the polymerization.