Polyphenylene sulfide-based heat-shrinkable tube and component covered with the tube
View Patent ↗The present invention provides a heat-shrinkable polyphenylene sulfide-based tube containing a resin composition (A) including a thermoplastic polyphenylene sulfide-based resin (a) as a main constituent, having a difference of 35° C. or more between the cold crystallization temperature Tc as measured by a differential scanning calorimetry in accordance with JIS-K7121 and the glass transition temperature Tg measured in the same manner, and having the glass transition temperature Tg between 65° C. and 85° C.; and the invention provides a component covered with the tube. The heat-shrinkable polyphenylene sulfide-based tube fulfills the characteristics required for a heat-shrinkable tube, such as heat resistance, low-temperature shrinkage characteristics, electrical characteristics, chemical resistance, and electrolytic solution resistance.
1. A polyphenylene sulfide based sulfide-comprising heat-shrinkable tube, comprising:
a resin composition (A) comprising a thermoplastic polyphenylene sulfide-based resin (a) as a main constituent,
wherein the tube has a difference of 35° C. or more between a cold crystallization temperature Tc and a glass transition temperature Tg measured by a differential scanning calorimetry in accordance with JIS-K7121, and
the glass transition temperature Tg of the tube is in a range of 65° C. or more and 85° C. or less.
2. The tube of claim 1 , exhibiting a flame retardancy VW-1 in accordance with evaluation by UL224 Optional VW-1 Flame Test and fracture energy of 0.2 J or more by a puncture impact test at 23° C.
3. The tube of claim 1 , having a heat shrinkage ratio in the case of immersion in warm water at 100° C. for 5 seconds is 30% or more and 70% or less in a radial direction, and 30% or less in a length direction.
4. The tube of claim 1 , wherein the resin composition (A) further comprises a thermoplastic elastomer (b).
5. The tube of claim 4 , wherein a content of the thermoplastic elastomer (b) is 0.5 mass % or more and 13 mass % or less with respect to 100 mass % of the resin composition (A).
6. The tube of claim 4 , wherein the resin composition (A) further comprises a plasticizer (c).
7. The tube of claim 6 , wherein the plasticizer (c) is a phosphorous-comprising plasticizer.
8. The tube of claim 7 , comprising a resin composition comprising:
80-95 mass % of the thermoplastic polyphenylene sulfide-comprising resin (a);
3-13 mass % of the thermoplastic elastomer (b); and
0.5-15 mass % of the phosphorous-comprising plasticizer (c),
with respect to the total 100 mass % of the thermoplastic polyphenylene sulfide-comprising resin (a), the thermoplastic elastomer (b), and the phosphorous-comprising plasticizer (c).
9. The tube of claim 6 , wherein a content of the thermoplastic elastomer (b) is 0.5 mass % or more and 13 mass % or less with respect to 100 mass % of the resin composition (A).
10. The tube of claim 6 , wherein a content of the plasticizer (c) is 0.5 mass % or more and 15 mass % or less with respect to 100 mass % of the resin composition (A).
11. The tube of claim 4 , having a heat shrinkage ratio in the case of immersion in warm water at 100° C. for 5 seconds is 30% or more and 70% or less in a radial direction, and 30% or less in a length direction.
12. The tube of claim 1 , wherein the resin composition (A) further comprises a plasticizer (c).
13. The tube of claim 12 , wherein the plasticizer (c) is a phosphorous-comprising plasticizer.
14. The tube of claim 12 , wherein a content of the plasticizer (c) is 0.5 mass % or more and 15 mass % or less with respect to 100 mass % of the resin composition (A).
15. The tube of claim 12 , having a heat shrinkage ratio in the case of immersion in warm water at 100° C. for 5 seconds is 30% or more and 70% or less in a radial direction, and 30% or less in a length direction.
16. The tube of claim 1 , wherein the resin composition (A) comprises at least one further thermoplastic resin (d), different from the thermoplastic polyphenylene sulfide-comprising resin (a).
17. The tube of claim 16 , wherein a content of the at least one further thermoplastic resin (d) is 0.5 mass % or more and 25 mass % or less with respect to 100 mass % of the resin, composition (A).
18. The tube of claim 1 , having a heat shrinkage ratio in the case of immersion in warm water at 90° C. for 5 seconds is 20% or more and 60% or less in a radial direction, and 25% or less in a length direction.
19. A component, covered with the tube of claim 1 .
20. The component of claim 19 , which is employed in an application of an electronic device or an electric device.