Woven geotextile fabric derived from beta-nucleated, polypropylene yarn or monofilament
View Patent ↗A woven geotextile fabric derived from beta-nucleated polyolefin yarn or monofilament, the method of manufacture of fabric, and the use of such fabric are disclosed. The yarn is made by compounding one or more polyolefins and a beta-nucleator reagent wherein the compounded mixture is extruded then drawn to at least 9 times its original length. The yarn or monofilament is woven into synthetic fabric useful for roadway construction, embankment stabilization, and mechanically stabilized earth.
1. A woven geotextile fabric comprising a beta-nucleated, stiff, highly drawn, yarn or monofilament having a rectangular cross-section made of an extrusion of polypropylene homopolymer and a beta-nucleator reagent selected from the group consisting of 5,12-dihydroquino[2,3-b]acridine-7,14-dione; isophthalic acid; terephthalic acid; the disodium salt of o-phthalic acid; an aluminum salt of 6-quinizarin sulfonic acid; N′, N′-dicyclohexyl-2,6-naphthalene dicarboxamide; and mixtures thereof wherein beta-crystallization of the yarn or monofilament is achieved by subjecting the extrusion to a temperature in the range of 190-220° F. for at least 2 seconds.
2. The woven geotextile fabric of claim 1 wherein the highly drawn, beta-nucleated polypropylene yarn or monofilament comprises a fill yarn.
3. The woven geotextile fabric of claim 1 wherein the highly drawn, beta-nucleated polypropylene yarn or monofilament comprises a warp yarn.
4. The woven geotextile fabric of claim 1 wherein the highly drawn, beta-nucleated polypropylene yarn or monofilament comprises both a fill yarn and a warp yarn.
5. The woven geotextile fabric of claim 1 comprising a weave selected from the group consisting of a plain weave, a twill weave, a satin weave, a half basket weave, and a crowfoot weave.
6. The woven geotextile fabric of claim 1 further comprising an additive selected from the group consisting of an opacifier, a pigment, a dye, a lubricant, an antistatic agent, an antioxidant, a UV absorber, and mixtures thereof.
7. The woven geotextile fabric of claim 1 wherein the highly drawn beta-nucleated yarn or monofilament has a denier in the range of 300 to 3000.
8. The woven geotextile fabric of claim 1 wherein the fabric comprises a plain weave.
9. A stiff, highly drawn beta-nucleated polymeric yarn or monofilament drawn at least nine times its original length comprising an extrusion of a polypropylene polymer and a beta-nucleator reagent selected from the group consisting of 5,12-dihydroquino[2,3-b]acridine-7,14-dione; isophthalic acid; terephthalic acid; the disodium salt of o-phthalic acid; an aluminum salt of 6-quinizarin sulfonic acid; N′, N′-dicyclohexyl-2,6-naphthalene dicarboxamide; and mixtures thereof wherein the yarn has a rectangular cross-section and exhibits a greater tenacity and greater tensile modulus than an otherwise identical yarn or monofilament that did not include the beta-nucleator reagent but was processed under identical conditions wherein beta-crystallization of the yarn or monofilament is achieved by subjecting the extrusion to a temperature in the range of 190-220° F. for at least 2 seconds.
10. The highly drawn polymeric yarn or monofilament of claim 9 wherein the polypropylene polymer comprises a polypropylene homopolymer.
11. The highly drawn polymeric yarn or monofilament of claim 9 wherein the propylene polymer comprises a copolymer of polypropylene and one or more other olefins.
12. The highly drawn polymeric yarn or monofilament of claim 9 wherein the propylene polymer comprises a polypropylene homopolymer, a copolymer, and mixtures thereof.
13. The highly drawn polymeric yarn or monofilament of claim 9 wherein the polypropylene polymer comprises a mixture of a polypropylene homopolymer with a melt flow rate of 4 g/10 minutes and a polypropylene impact copolymer with a melt flow rate of 0.8 g/10 minutes.
14. The highly drawn polymeric yarn or monofilament of claim 9 further comprising an additive selected from the group consisting of an opacifier, a pigment, a dye, a lubricant, an antistatic agent, an antioxidant, a UV absorber, and mixtures thereof.
15. The highly drawn polymeric yarn or monofilament of claim 14 wherein the additive comprises carbon black.
16. The highly drawn polymeric yarn or monofilament of claim 9 wherein the beta-nucleator reagent comprises 5,12-dihydroquino[2,3-b]acridine-7,14-dione.
17. The highly drawn polymeric yarn or monofilament of claim 9 wherein the beta-nucleator reagent is present in the range of about 0.5 to about 5000 ppm.