Compositions and methods for treating cellulose based materials with micronized additives
View Patent ↗A composition for treating cellulosic materials is provided. The composition comprises a dispersion of micronized additives. The dispersion comprises additive particles with diameters in the range of 0.001 to 25 microns. Also provided is a method for the application of the additive-containing composition to wood, as well as wood products which have been treated with the composition.
1. A process for treating wood, said process comprising the steps of:
a) providing an aqueous composition comprising one or more solid particles of an additive dispersed in water having diameters in the range of 0.001 to 25 microns;
b) applying said composition to wood such that at least some of the particles penetrate the surface of the wood and are distributed throughout a cross section of the wood;
wherein the additive is an iron oxide; greater than 80 weight percent of the particles have diameters less than 1 micron; and the additive is applied to the wood by pressure treatment, vacuum treatment or both.
2. A process as in claim 1 , wherein said aqueous composition further comprises one or more additives selected from the group consisting of carbon black, titanium dioxide, parafin wax, acrylic polymer, and zinc borate.
3. A process as in claim 1 , further comprising performing the step a) by grinding said additive into micronized form.
4. Wood treated by the process of claim 1 , wherein said wood comprises solid iron oxide particles inside the wood, wherein said iron oxide particles have diameters in the range of from 0.001 to 25 microns.
5. Wood as in claim 4 , wherein said aqueous composition further comprises one or more additives selected from the group consisting of inorganic pigments, organic pigments, water repellants, anti-weathering agents, dimensional stabilization agents and fire retardants.
6. Wood as in claim 4 wherein said aqueous composition further comprises one or more additives selected from the group consisting of carbon black, titanium dioxide, parafin wax, acrylic polymer, and zinc borate.
7. Wood comprising:
a) an aqueous composition comprising one or more solid particles of an additive dispersed in water having diameters in the range of 0.001 to 25 microns;
b) wherein at least some of the particles penetrate the surface of the wood and are distributed throughout a cross section of the wood;
c) wherein the additive is an iron oxide; and greater than 80 weight percent of the particles have diameters less than 1 micron.
8. Wood of claim 7 , wherein said aqueous composition further comprises one or more additives selected from the group consisting of carbon black, titanium dioxide, parafin wax, acrylic polymer, and zinc borate.
9. A process as in claim 1 , wherein said aqueous composition further comprises a biocide.
10. A process as in claim 9 , wherein said biocide is solid.
11. A process as in claim 10 , wherein said solid biocide is copper or a copper compound.
12. Wood of claim 7 , wherein said aqueous composition further comprises a biocide.
13. Wood of claim 12 , wherein said biocide is solid.
14. Wood of claim 13 , wherein said solid biocide is copper or a copper compound.
15. A process as in claim 1 , wherein said aqueous composition further comprises a colorant.
16. Wood of claim 7 , wherein said aqueous composition further comprises a colorant.