Method of preparing nitrogen-doped graphene and nitrogen-doped graphene prepared thereby
View Patent ↗The present invention relates to a method of preparing a nitrogen-doped graphene comprising preparing a Edge-Functionalized Graphene by binding a graphite with a organic material having amino groups and functional groups such as carboxy acid group through an electrophilic substitution reaction, and heat treating the resultant Edge-Functionalized Graphene, and a nitrogen-doped graphene prepared thereby. According to the present invention, by a more inexpensive and simpler method, a nitrogen-doped graphene can be prepared at higher purity and higher yield. The nitrogen-doped graphene obtained by the present invention has very excellent physical and electric properties, and particularly has a superior oxygen reduction capability, compared with the platinum catalyst used at cathode of a H 2 /O 2 fuel cell so that it will replace the platinum to lower more the cost of a H 2 /O 2 fuel cell or to increase its life and further to provide a new turning point for the commercialization of a H 2 /O 2 fuel cell.
1. A method of preparing nitrogen doped-graphene comprising 1) reacting an organic material having one or more amino groups and one or more functional groups selected from the group consisting of carboxylic acid group, amide group, sulfonic acid group, carbonylchloride group and carbonylbromide group with graphite in a reaction medium containing polyphosphoric acid and phosphorus pentoxide-, thereby the graphite being exfoliated with the functional group of the organic material grafted to the graphite to prepare organic material-grafted graphene; and 2) heat treating the prepared organic material-grafted graphene at a temperature of 300 to 1,200° C.
2. The method of preparing nitrogen-doped graphene according to claim 1 , wherein the organic material is alkane having 1 to 13 carbon atoms, alkene having 2 to 13 carbon atoms, alkyne having 2 to 13 cabon atoms, cycloalkane having 3 to 13 carbon atoms, arene having 7 to 19 carbon atoms or arylalkane having 7 to 19 carbon atoms, which have amino groups and the above functional groups, wherein the alkane, the alkene, the alkyne, the cycloalkane, the arene and the arylalkane are unsubstituted or substituted with a substituent selected from the group consisting of halo, nitro, amino, cyano, mercapto, hydroxy, alkyl having 1 to 4 carbon atoms, alkoxy having 1 to 4 carbon atoms, formyl, alkylcarbonyl having 1 to 4 carbon atoms, phenyl, benzoyl, and phenoxy or the combination thereof.
3. The method of preparing nitrogen-doped graphene according to claim 1 , wherein the organic material is aminobenzoic acid, diaminobenzoic acid, aminobenzoamide or diaminobenzoamide, which are unsubstituted or substituted with a substituent selected from the group consisting of halo, nitro, amino, cyano, mercapto, hydroxy, alkyl having 1 to 4 carbon atoms, alkoxy having 1 to 4 carbon atoms, formyl, alkylcarbonyl having 1 to 4 carbon atoms, phenyl, benzoyl, and phenoxy or the combination thereof.
4. The method of preparing nitrogen-doped graphene according to claim 1 , wherein the organic material is a compound selected from the group consisting of 3-aminobenzoic acid, 4-aminobenzoic acid, 3-(4-aminophenyl)benzoic acid, 3-(3-aminophenyl)benzoic acid, 4-(4-aminophenyl)benzoic acid, 4-(3-aminophenyl)benzoic acid, 5-aminoisophthalic acid, 3-(4-aminophenoxy)benzoic acid, 3-(3-aminophenoxy)benzoic acid, 4-(4-aminophenoxy)benzoic acid, 4-(3-aminophenoxy)benzoic acid, 3,4-diaminobenzoic acid, 3,5-diaminobenzoic acid, 3-aminobenzoamide and 4-aminobenzoamide.
5. The method of preparing nitrogen-doped grapheme according to claim 1 , wherein the heat-treatment is conducted for 10 minutes to 12 hours.
6. The method of preparing nitrogen-doped graphene according to claim 1 , wherein the heat-treatment is conducted under the atmosphere of gas selected from the group consisting of methane, hydrogen, nitrogen, helium, neon and argon or the combination thereof.