Microporous carbon and method for making the same
View Patent ↗A substantially homogeneous composite for making a carbon material includes a carbon precursor and an activation agent that is soluble in a solution including the carbon precursor. An amount of the activation agent used is sufficient to form the carbon material having at least 90% of a total pore volume of the carbon material composed of micropores, and 10% or less of the total pore volume composed of mesopores and macropores.
1. A method for making microporous carbon, comprising:
preparing a carbon precursor solution consisting of:
a carbon precursor chosen from phenolic resin oligomers, resorcinol, and phloroglucinol based resin oligomers; and
a liquid medium selected from the group consisting of water, and a mixture of water and an alcohol;
selecting an activation agent that is soluble in the carbon precursor solution, the activation agent being chosen from potassium hydroxide, sodium hydroxide, potassium carbonate, and sodium carbonate;
mixing the activation agent in the carbon precursor solution to form a substantially homogeneous mixture of the activation agent dissolved in the carbon precursor solution;
then heating the substantially homogeneous mixture of the activation agent dissolved in the carbon precursor solution, thereby polymerizing the substantially homogeneous mixture and forming a substantially homogeneous composite; and
substantially simultaneously carbonizing and activating the substantially homogeneous composite.
2. The method as defined in claim 1 wherein the carbon precursor solution is prepared by reacting phenol with formaldehyde in the liquid medium in the presence of a catalyst.
3. The method as defined in claim 1 , further comprising mixing a controlled amount of the activation agent in the carbon precursor solution to control a surface area of the microporous carbon.
4. The method as defined in claim 1 wherein mixing includes stirring the activation agent in the carbon precursor solution.
5. The method as defined in claim 1 wherein carbonizing and activating are accomplished by heating the substantially homogeneous composite to a temperature ranging from about 500° C. to about 900° C. under an inert atmosphere for a predetermined time period ranging from about 0.5 hours to about 8 hours.
6. The method as defined in claim 1 , further comprising washing the substantially homogeneous carbonized composite.