Process for making a stiffened paper
View Patent ↗A process for making a stiffened and rigid paper includes preparing a pulp slurry consisting essentially of water, a cellulosic pulp, a crosslinker, and a starch, and optionally a binder; draining the liquid from the pulp slurry to form a web; and drying the web. Alternatively, a process for making a stiffened and rigid paper includes the step of adding at least one crosslinker at one or more locations, such as at the wet-end, dry-end, or at both ends of the papermaking process. Suitable crosslinkers include a glyoxal-containing crosslinker, a gluteraldehyde, a polyfunctional aziridine, a zirconium-containing crosslinker, a titanium-containing crosslinker, and an epichlorohydrin, and mixtures thereof. When a binder is employed, it can be added either in the dry or wet form. Provided is a neutral or alkaline process to produce a paper product having the improved mechanical properties of a laminated product in the Z-direction, without a lamination step.
1. A process for making a stiffened and rigid paper, the process consisting essentially of:
(i) preparing a pulp slurry consisting essentially of water, a cellulosic pulp, and a starch, and optionally a binder;
(ii) draining the liquid from the pulp slurry to form a web;
(iii) adding at least one crosslinker in an amount of from about 0.3 weight percent to about 10 weight percent based on a weight of total solids of the pulp slurry; and
(iv) drying the web to produce a paper product having a basis weight of about 60 lbs./3300 ft 2 to about 400 lbs./3300 ft 2 .
2. The process of claim 1 , wherein the at least one crosslinker is added by spraying the crosslinker onto the web.
3. The process of claim 1 , wherein the at least one crosslinker is added at a sizepress.
4. The process of claim 1 , wherein the at least one crosslinker is added by spraying the crosslinker onto the web and added at a sizepress.
5. The process of claim 1 , wherein the at least one crosslinker is selected from the group consisting of a glyoxal-containing crosslinker, a gluteraldehyde, a polyfunctional aziridine, a zirconium-containing crosslinker, a titanium-containing crosslinker, and an epichlorohydrin, and mixtures thereof.
6. The process of claim 1 , wherein the at least one crosslinker is a glyoxal-containing crosslinker.
7. The process of claim 1 , wherein adding the at least one crosslinker comprises first forming a crosslinker slurry and then adding the crosslinker slurry to the web.
8. The process of claim 1 , wherein the pulp slurry includes the binder.
9. The process of claim 8 , wherein the binder is polyvinyl alcohol (PVOH).
10. The process of claim 8 , wherein the binder is selected from the group consisting of starch, casein, protein binders, carboxymethyl cellulose (CMC), polyvinyl alcohol (PVOH), Gum products, and gelatins, and mixtures thereof.
11. The process of claim 1 , wherein the crosslinker is added in an amount effective to provide an unlaminated sheet of paper having a stiffness of within 10% of, and a rigidity at least equal to, an equal caliper laminated sheet for a basis weight in the range of 60 lbs/3300 ft^2 to 400 lbs/3300 ft^2.
12. The process of claim 1 , wherein the crosslinker is present in the web in an amount of at least about 1.5 weight percent based on the weight of solids in the web.
13. The process of claim 1 , wherein the crosslinker is present in the web in an amount between about 0.5 to about 5 weight percent based on the weight of solids in the web.
14. The process of claim 1 , wherein the at least one crosslinker is present at an amount of 60 to 200 lbs, of crosslinker per ton of dry paper pulp.
15. The process of claim 1 , wherein the binder is polyvinyl alcohol (PVOH), and the binder is present in an amount between about 0.1 weight percent and about 5 weight percent based on the weight of the total solids.
16. A process for making a stiffened and rigid paper, the process consisting of:
(i) preparing a pulp slurry consisting of water, a cellulosic pulp, a starch, and optionally a binder;
(ii) draining the liquid from the pulp slurry to form a web;
(iii) adding at least one crosslinker; and
(iv) drying the web to produce a paper product.