Composition for dyeing of cellulosic fabric
View Patent ↗A method of making a composition for spray application onto surfaces of a cotton fabric includes mixing together a wetter, a reactive dye and water to form a first solution, adding a thickener into the first solution for between about five minutes and sixty minutes to form a partial composition, and adding an alkali with the partial composition to complete the composition.
1. A method of making a solution for spray application onto surfaces of a cotton fabric, consisting of:
mixing together a wetter, a reactive dye and water to form a solution, the wetter being selected from the group consisting of a first surfactant, wherein the first surfactant is a blend of sulfuric acid disodium salt and phosphoric acid trisodium salt, and a second surfactant, wherein the second surfactant is sodium dioctyl sulfosuccinate;
adding a thickener to the solution; and
adding an alkali to the solution at a time that allows spray application of the solution onto the surfaces of a cotton fabric before the reactive dye hydrolyzes, the alkali being selected from the group consisting of a first combination of soda ash, potassium carbonate and phosphate, and a second combination of sodium silicate and a caustic.
2. The method of claim 1 , wherein the wetter, the reactive dye, the thickener, and the alkali are anionic or non-ionic.
3. The method of claim 1 , wherein the wetter is added in an amount between 5 g/l and 40 g/l.
4. The method of claim 1 , wherein the reactive dye is an azo metal complex or dioxazine.
5. The method of claim 4 , wherein the reactive dye is added in an amount between 10 g/l and 80 g/l.
6. The method of claim 1 , wherein the step of adding the thickener is blending the thickener into the solution at a high speed.
7. The method of claim 6 , wherein the thickener is blended into the solution for between 5 minutes and 60 minutes.
8. The method of claim 7 , wherein the thickener is added in an amount between 5 g/l and 50 g/l.
9. The method of claim 8 , wherein the thickener is an acrylic acid copolymer.
10. The method of claim 9 , wherein the acrylic copolymer has between 2 percent and 3 percent napthal spirits.
11. The method of claim 1 , wherein the alkali is added in an amount between 3 g/l and 20 g/l.
12. The method of claim 11 , wherein the alkali has a pH between 10.5 and 11.7.
13. A method of making and applying a solution for spray application onto surfaces of a cotton fabric, consisting of:
mixing together a wetter, a reactive dye, a thickener, an alkali, and water in an in-line sleeve to form a solution;
the wetter being selected from the group consisting of a first surfactant, wherein the first surfactant is a blend of sulfuric acid disodium salt and phosphoric acid trisodium salt, and a second surfactant, wherein the second surfactant is sodium dioctyl sulfosuccinate;
the alkali being selected from the group consisting of a first combination of soda ash, potassium carbonate and phosphate, and a second combination of sodium silicate and a caustic; and
moving the solution from the in-line sleeve to a spray head for application of the solution onto the surfaces of the cotton fabric before the reactive dye hydrolyzes.
14. The method of claim 13 , wherein the in-line sleeve has a mixer therein.
15. The method of claim 14 , wherein the mixer is a corkscrew configuration.
16. The method of claim 13 , wherein application onto the fabric is spraying two sides of the fabric between 5 and 20 seconds.
17. The method of claim 13 , wherein the wetter, the reactive dye, the thickener, and the alkali are anionic or non-ionic.
18. The method of claim 13 , wherein the wetter is added in an amount between 5 g/l and 40 g/l.
19. The method of claim 13 , wherein the reactive dye is an azo metal complex or dioxazine.
20. The method of claim 19 , wherein the reactive dye is added in an amount between 10 g/l and 80 g/l.
21. The method of claim 13 , wherein the thickener is added in an amount between 5 g/l and 50 g/l.
22. The method of claim 21 , wherein the thickener is an acrylic acid copolymer.
23. The method of claim 22 wherein the acrylic copolymer has between 2 percent and 3 percent napthal spirits.
24. The method of claim 13 , wherein the alkali is added in an amount between 3 g/l and 20 g/l.
25. The method of claim 24 , wherein the alkali has a pH between 10.5 and 11.7.