A method is disclosed of manufacturing a transparent wear resistant surface layer ( 1 ). The method may include the steps of, applying a decorative material on a carrier, applying a dry powder layer comprising a mix of processed wood fibers, binder and wear resistant particles above the decorative layer, curing the mix to a decorative surface, including the transparent wear resistant layer, by applying heat and pressure on the mix. In a preferred embodiment the method includes the step of pressing the mix against an embossed matrix to create an embossed decorative surface with high wear resistance.
1. A method of manufacturing a building panel, wherein the method comprises the steps of:
applying a decorative layer on a carrier;
applying a dry powder layer, comprising a mix of processed wood fibres, binder and wear resistant particles, on the decorative layer; and
curing the mix by applying heat and pressure to obtain a decorative surface layer comprising a transparent wear resistant layer.
2. The method as claimed in claim 1 , wherein the panel is a floor panel.
3. The method as claimed in claim 1 , wherein the carrier is a wood based board.
4. The method as claimed in claim 1 , wherein the carrier is an HDF or MDF board.
5. The method as claimed in claim 1 , wherein the wear resistant particles are aluminium oxide.
6. The method as claimed in claim 1 , wherein the decorative layer is a printed paper.
7. The method as claimed in claim 1 , wherein the curing step comprises pressing the mix against an embossed matrix.
8. The method as claimed in claim 7 , wherein the pressing against the embossed matrix creates an embossing depth that exceeds a thickness of the decorative layer.
9. The method as claimed in claim 7 , wherein the pressing against the embossed matrix creates an embossing depth that exceeds the combined thickness of the decorative layer and the transparent wear layer.
10. A method of manufacturing a building panel, wherein the method comprises the steps of:
applying a decorative layer on a carrier, wherein the decorative layer comprises a transparent paper based overlay comprising aluminium oxide;
applying a dry powder layer, comprising a mix of processed wood fibres, binder and wear resistant particles, on the decorative layer; and
curing the mix by applying heat and pressure to obtain a decorative surface layer comprising a transparent wear resistant layer.
11. A method of manufacturing a building panel, wherein the method comprises the steps of:
applying a decorative layer on a carrier, wherein the decorative layer comprises a transparent paper based overlay comprising aluminium oxide applied over a lower dry powder layer, the lower dry powder layer comprising wood fibres and a binder;
applying a dry powder layer, comprising a mix of processed wood fibres, binder and wear resistant particles, on the decorative layer; and
curing the mix by applying heat and pressure to obtain a decorative surface layer comprising a transparent wear resistant layer.
12. The method as claimed in claim 1 , wherein the processed wood fibres are essentially all smaller than 1.0 mm.
13. The method as claimed in claim 1 , wherein the processed wood fibres are essentially all smaller than 0.5 mm.
14. The method as claimed in claim 1 , wherein the heat and pressure is applied for 5-200 seconds.
15. The method as claimed in claim 1 , wherein the heat and pressure is applied for 5-30 seconds.
16. The method as claimed in claim 1 , wherein the heat applied is in the range of about 140° C. to about 200° C.
17. The method as claimed in claim 1 , wherein the pressure applied is in the range of about 20 to about 60 kg/cm2.
18. The method as claimed in claim 1 , wherein the thickness of the transparent surface layer exceeds the thickness of the decorative layer.
19. The method as claimed in claim 1 , wherein the decorative surface layer is embossed and the thickness of the transparent surface layer varies such that the thickness in an upper portion exceeds a thickness of a lower portion.
20. The method as claimed in claim 1 , wherein the heat and pressure is applied for 5-30 seconds, the heat applied is in the range of about 140° C. to about 200° C., and the pressure applied is in the range of about 20 to about 60 kg/cm2.
21. The method as claimed in claim 1 , wherein the decorative layer is applied on the carrier before the dry powder layer is applied on the decorative layer.