Precipitation hardenable martensitic stainless steel and steam turbine blade using the same
View Patent ↗A precipitation hardenable martensitic stainless steel excellent in the stability of martensite, having the high strength, high toughness and high corrosion resistance is provided. The precipitation hardenable martensitic stainless steel contains at a mass rate, C: 0.05-0.10%, Cr: 12.0-13.0%, Ni: 6.0-7.0%, Mo: 1.0-2.0%, Si: 0.01-0.05%, Mn: 0.06-1.0%, Nb: 0.3-0.5%, V: 0.3-0.5%, Ti: 1.5-2.5%, Al: 1.0-2.3%, and the remainder consisting of Fe and an unavoidable impurity.
1. A precipitation hardenable martensitic stainless steel containing at a mass rate, C: 0.05-0.10%, Cr: 12.0-13.0%, Ni: 6.0-7.0%, Mo: 1.0-2.0%, Si: 0.01-0.05%, Mn: 0.06-1.0%, Nb: 0.3-0.5%, V: 0.3-0.5%, Ti: 1.5-2.5%, Al: 1.0-2.3%, and the remainder consisting of Fe and an unavoidable impurity, wherein
the precipitation hardenable martensitic stainless steel satisfies all conditions that a value of (a) defined in the equation below is in the range of 1.1 to 1.8, a value of (b) is in the range of 8.5 to 11.8, a value of (c) is 20.2 or less, and a value of (d) is 10.0 or less
( a )=[Nb %]+[V %]+10×[C %]
( b )=[Al %]+[Ni %]+[Ti %]
( c )=[Cr %]+1.5×[Si %]+[Mo %]+0.5×[Nb %]+2×[Ti %]
( d )=[Ni %]+0.5×[Mn %]+30×[C %].
2. A steam turbine blade formed by a precipitation hardenable martensitic stainless steel containing at a mass rate, C: 0.05-0.10%, Cr: 12.0-13.0%, Ni: 6.0-7.0%, Mo: 1.0-2.0%, Si: 0.01-0.05%, Mn: 0.06-1.0%, Nb: 0.3-0.5%, V: 0.3-0.5%, Ti: 1.5-2.5%, Al: 1.0-2.3%, and the remainder consisting of Fe and an unavoidable impurity, wherein
the precipitation hardenable martensitic stainless steel satisfies all conditions that a value of (a) defined in the equation below is in the range of 1.1 to 1.8, a value of (b) is in the range of 8.5 to 11.8, a value of (c) is 20.2 or less, and a value of (d) is 10.0 or less,
( a )=[Nb %]+[V %]+10×[C %]
( b )=[Al %]+[Ni %]+[Ti %]
( c )=[Cr %]+1.5×[Si %]+[Mo %]+0.5×[Nb %]+2×[Ti %]
( d )=[Ni %]+0.5×[Mn %]+30×[C %].
3. The steam turbine blade according to claim 2 , wherein the steam turbine blade is a final stage blade of a low pressure steam turbine.
4. The steam turbine blade according to claim 3 , wherein a length of the steam turbine blade is 45 inch (1.14 m) or more for a rotational speed of 3600 rpm and the length of the steam turbine blade is 50 inch (1.27 m) or more for a rotational speed of 3000 rpm.