Nanoscale ion storage materials including co-existing phases or solid solutions
View Patent ↗Nanoscale ion storage materials are provided that exhibit unique properties measurably distinct from their larger scale counterparts. For example, the nanoscale materials can exhibit increased electronic conductivity, improved electromechanical stability, increased rate of intercalation, and/or an extended range of solid solution. Useful nanoscale materials include alkaline transition metal phosphates, such as LiMPO 4 , where M is one or more transition metals. The nanoscale ion storage materials are useful for producing devices such as high energy and high power storage batteries, battery-capacitor hybrid devices, and high rate electrochromic devices.
1. A lithium transition metal phosphate material for use as a positive electroactive material in a lithium ion battery having a specific surface area of at least about 20 m 2 /g and comprising only one transition metal, said lithium transition metal phosphate and said surface area selected to provide at least two co-existing olivine phases during cycling of the battery, wherein the two co-existing olivine phases include a lithium-rich transition metal phosphate phase and a lithium-poor transition metal phosphate phase, wherein the percentage molar volume difference between the two phases is less than about 6.4%.
2. The lithium transition metal phosphate material of claim 1 , wherein the percentage molar volume difference between the two phases is less than about 6.25%.
3. The lithium transition metal phosphate material of claim 1 , wherein the percentage molar volume difference between the two phases is less than about 5.75%.
4. The lithium transition metal phosphate material of claim 1 , wherein the percentage molar volume difference between the two phases is less than about 5.5%.
5. The lithium transition metal phosphate material of claim 1 , wherein each of the two co-existing phases is crystalline and is defined by a unit cell having three lattice parameters, and wherein the differences in at least two of the three lattice parameters between the two unit cells are less than 3%.
6. The lithium transition metal phosphate material of claim 5 , wherein the differences in all lattice parameters between the two unit cells are less than 4.7%.
7. The lithium transition metal phosphate material of claim 5 , wherein the differences in all lattice parameters between the two unit cells are less than 4.5%.
8. The lithium transition metal phosphate material of claim 5 , wherein differences in all lattice parameters between the two unit cells are less than 4.0%.
9. The lithium transition metal phosphate material of claim 5 , wherein the differences in all lattice parameters between the two unit cells are less than 3.5%.
10. The lithium transition metal phosphate material of claim 5 , wherein the two co-existing phases have a crystallographic plane in which the misfit strain between the two phases is less than about 1.6%.
11. The lithium transition metal phosphate material of claim 10 , wherein the misfit strain between the two phases is less than about 1.5%.
12. The lithium transition metal phosphate material of claim 10 , wherein the misfit strain between the two phases is less than about 1.4%.
13. The lithium transition metal phosphate material of claim 10 , wherein none of the planes formed by any two of the lattice parameters of a unit cell of the crystal have a misfit strain between the two phases exceeding 8%.
14. The lithium transition metal phosphate material of claim 13 , wherein none of the planes formed by any two of the lattice parameters of a unit cell of the crystal have a misfit strain between the two phases exceeding 7.5%.
15. The lithium transition metal phosphate material of claim 13 , wherein none of the planes formed by any two of the lattice parameters of a unit cell of the crystal have a misfit strain between the two phases exceeding 6.0%.
16. The lithium transition metal phosphate material of claim 1 , wherein the material has a specific surface area of at least about 25 m 2 /g.
17. The lithium transition metal phosphate material of claim 1 , wherein the material has a specific surface area of at least about 30 m 2 /g.
18. The lithium transition metal phosphate material of claim 1 , wherein the material has a specific surface area of at least about 35 m 2 /g.
19. The lithium transition metal phosphate material of claim 1 , wherein the material has a specific surface area of at least about 40 m 2 /g.
20. The lithium transition metal phosphate material of claim 1 , wherein the material has a specific surface area of at least about 50 m 2 /g.
21. The lithium transition metal phosphate material of claim 1 , wherein material has an overall composition of Li 1-x MPO 4 , where M comprises one first row transition metal selected from the group consisting of Ti, V, Cr, Mn, Fe, Co and Ni, and wherein in use x ranges from 0 to 1.
22. The lithium transition metal phosphate material of claim 21 , wherein the composition is lithium iron phosphate.
23. The lithium transition metal phosphate material of claim 21 , wherein the material exhibits a solid solution at room temperature over a composition range of 0<x<0.3, and/or 0.8<x<1.
24. The lithium transition metal phosphate material of claim 21 , wherein the material exhibits a stable solid solution at room temperature over a composition range of x between 0 and at least about 0.15 and/or 0.9<x<1.
25. The lithium transition metal phosphate material of claim 21 , wherein the material exhibits a stable solid solution at room temperature over a composition range of x between 0 and at least about 0.07 and/or 0.95<x<1.
26. The lithium transition metal phosphate material of claim 21 , wherein the lithium-rich transition metal phosphate phase has the composition Li y MPO 4 exhibiting a stable solid solution at room temperature and the lithium-poor transition metal phosphate phase has the composition Li 1-x MPO 4 exhibiting a stable solid solution at room temperature, wherein 0.02<y<0.2 and 0.02<x<0.3.
27. The lithium transition metal phosphate material of claim 26 , wherein the solid solution occupies a fraction of the compositional range of lithium defined as y+x.
28. The lithium transition metal phosphate material of claim 1 , wherein material has an overall composition of Li 1-x-z M 1-z PO 4 , where M comprises one first row transition metal selected from the group consisting of Ti, V, Cr, Mn, Fe, Co and Ni, where x is from 0 to 1 and z can be positive or negative.
29. The lithium transition metal phosphate material of claim 28 , wherein the composition is lithium iron phosphate.
30. The lithium transition metal phosphate material of claim 28 , where z is between about 0.15 and −0.15.
31. The lithium transition metal phosphate material of claim 1 , wherein the material is of a form selected from the group consisting of particles, agglomerated particles, fibers and coatings.
32. The lithium transition metal phosphate material of claim 31 , wherein the form has an average smallest cross-sectional dimension of about 75 nm or less.
33. The lithium transition metal phosphate material of claim 31 , wherein the average smallest cross-sectional dimension is about 60 nm or less.
34. The lithium transition metal phosphate material of claim 31 , wherein the average smallest cross-sectional dimension is about 45 nm or less.
35. The lithium transition metal phosphate material of claim 1 , wherein the material is in the form of agglomerated particles and the average crystallite size as determined by x-ray diffraction is less than about 800 nm.
36. The lithium transition metal phosphate material of claim 35 , wherein the average crystallite size as determined by x-ray diffraction is less than about 600 nm.
37. The lithium transition metal phosphate material of claim 35 , wherein the average crystallite size as determined by x-ray diffraction is less than about 500 nm.
38. The lithium transition metal phosphate material of claim 35 , wherein the average crystallite size as determined by x-ray diffraction is less than about 300 nm.
39. The lithium transition metal phosphate material of claim 1 , wherein the materials is crystalline.
40. The lithium transition metal phosphate material of claim 1 , wherein the material is amorphous.
41. A cathode comprising the material of claim 1 .
42. An electrochemical cell comprising the electrode of claim 41 .
43. A cathode comprising the material of claim 21 .
44. An electrochemical cell comprising the electrode of claim 43 .
45. The lithium transition metal phosphate material of claim 1 , wherein the material comprises disordered olivine formed upon delithiation or lithiation.
46. The lithium transition metal phosphate material of claim 1 , wherein the material comprises a lithium-deficient lithium transition metal phosphate solid solution formed upon delithiation at a temperature below 150° C.
47. The lithium transition metal phosphate material of claim 46 , wherein the lithium-deficient lithium transition metal phosphate solid solution comprises an ordered olivine structure.
48. The lithium transition metal phosphate material of claim 47 , wherein the deficiency occurs on the lithium or M1 sites of the ordered olivine.
49. The lithium transition metal phosphate material of claim 47 , wherein a disorder occurs on the lithium or M1 sites of the ordered olivine.
50. The lithium transition metal phosphate material of claim 1 , wherein the material transforms upon first charge to disordered olivine having a lithium deficient solid solution and retains such solid solution at temperatures below 150° C.
51. The lithium transition metal phosphate material of claim 50 retaining the solid solution at temperatures below 100° C.
52. The lithium transition metal phosphate material of claim 50 retaining the solid solution at temperatures below 50° C.