Bonding wood composites with resin solids-fortified phenol-formaldehyde resin
View Patent ↗The invention comprises an aqueous phenol-formaldehyde resole resin liquid fortified with powdered (e.g., spray dried) phenol-formaldehyde resole resin, preparing wood composites, particularly oriented strand board (OSB), waferboard, particleboard, medium density fiber board, and hardboard, using the solids-fortified liquid resin, and related wood composites bonded with the solids-fortified resin.
1. An adhesive binder formulation comprising a fluid mixture of an aqueous phenol-formaldehyde resole resin liquid and a powdered phenol-formaldehyde resole resin, wherein the powdered phenol-formaldehyde resole resin is dispersed in the aqueous phenol-formaldehyde resole resin liquid,
wherein the powdered phenol-formaldehyde resole resin is in an amount of from 0.2 to 10% by weight.
2. An adhesive binder formulation consisting essentially of a fluid mixture of an aqueous phenol-formaldehyde resole resin liquid and a powdered phenol-formaldehyde resole resin, wherein the powdered phenol-formaldehyde resole resin is dispersed in the aqueous phenol-formaldehyde resole resin liquid,
wherein the powdered phenol-formaldehyde resole resin is in an amount of from 0.2 to 10% by weight.
3. The adhesive binder formulation according to claim 1 or 2 wherein the powdered phenol-formaldehyde resole resin is dispersed in the aqueous phenol-formaldehyde resole resin liquid in an amount of from 0.2 to 5% by weight of dissolved solids in the aqueous phenol-formaldehyde resole resin liquid.
4. The adhesive binder formulation according to claim 3 wherein aqueous phenol-formaldehyde resole resin liquid has a total alkalinity in the range of 2 to 7 percent by weight.
5. The adhesive binder formulation according to claim 4 wherein the powdered phenol-formaldehyde resole resin is prepared by spray drying an aqueous, alkaline phenol-formaldehyde resole resin composition.
6. A wood composite comprising wood substrates bound together by a cured, adhesive binder formulation of claim 1 .
7. A wood composite comprising wood pieces bound together by a cured, adhesive binder formulation of claim 2 .
8. A method of making a wood composite comprising applying an adhesive binder formulation to wood substrates, wherein the adhesive binder formulation comprises a fluid mixture of an aqueous phenol-formaldehyde resole resin liquid and a powdered phenol-formaldehyde resole resin, wherein the powdered phenol-formaldehyde resole resin is dispersed in the aqueous phenol-formaldehyde resole resin liquid, wherein the powdered phenol-formaldehyde resole resin is in an amount of from 0.2 to 10% by weight and consolidating the wood substrates with the applied the adhesive binder formulation under conditions to produce the wood composite.
9. A method of making a wood composite according to claim 8 wherein the adhesive binder formulation is mixed with wood pieces; forming the wood pieces into a mat and consolidating the mat, through the application of heat and pressure, into the wood composite.