Seamless steel pipe and method for manufacturing the same
A seamless steel pipe of a low-alloy steel consisting, by mass %, of C: 0.10 to 0.20%, Si: 0.05 to 1.0%, Mn: 0.05 to 1.2%, Ni: 0.02 to 1.5%, Cr: 0.50 to 1.50%, Mo: 0.50 to 1.50%, Nb: 0.002 to 0.10%, Al: 0.005 to 0.10%, and either or both of Ti: 0.003 to 0.050% and V: 0.01 to 0.20%, the balance being Fe and impurities, the impurities containing 0.025% or less of P, 0.005% or less of S, 0.007% or less of N, and less than 0.0003% of B, wherein the tensile strength is 950 MPa or more and the yield strength is 850 MPa or more, and the Charpy absorbed energy at −40° C. is 60 J or more. This seamless steel pipe may further contain one or more of Cu: 0.02 to 1.0%, Ca: 0.0005 to 0.0050%, and Mg: 0.0005 to 0.0050%. The present invention also provides a method for manufacturing the above-described seamless steel pipe.
1. A seamless low-alloy steel pipe comprising, in percent by mass, C: 0.10 to 0.18%, Si: 0.05 to 1.0%, Mn: 0.05 to 1.2%, Ni: 0.05 to 1.5%, Cr: 0.50 to 1.50%, Mo: 0.50 to 1.50%, Nb: 0.002 to 0.10%, Al: 0.005 to 0.10%, and either or both of Ti: 0.003 to 0.050% and V: 0.01 to 0.20%, the balance being Fe and impurities, the impurities containing 0.025% or less of P, 0.005% or less of S, 0.007% or less of N, and less than 0.0003% of B, wherein a wall thickness of the pipe is 20 mm or more, the tensile strength is 950 MPa or more and the yield strength is 850 MPa or more, and the Charpy absorbed energy at −40° C. is 60 J or more.
2. The seamless low-alloy steel pipe according to claim 1 , which further contains either or both of Ca: 0.0005 to 0.0050% and Mg: 0.0005 to 0.0050%.
3. A seamless low-alloy steel pipe comprising, in percent by mass, C: 0.10 to 0.18%, Si: 0.05 to 1.0%, Mn: 0.05 to 1.2%, Ni: 0.02 to 1.5%, Cr: 0.50 to 1.50%, Mo: 0.50 to 1.50%, Nb: 0.002 to 0.10%, Cu: 0.02 to 1.0% Al: 0.005 to 0.10%, and either or both of Ti: 0.003 to 0.050% and V: 0.01 to 0.20%, the balance being Fe and impurities, the impurities containing 0.025% or less of P, 0.005% or less of S, 0.007% or less of N, and less than 0.0003% of B,
wherein the wall thickness is 20 mm or more, the tensile strength is 950 MPa or more and the yield strength is 850 MPa or more, and the Charpy absorbed energy at −40° C. is 60 J or more.
4. The seamless steel pipe according to claim 3 , which further contains either or both of Ca: 0.0005 to 0.0050% and Mg: 0.0005 to 0.0050%.
5. A method for manufacturing a seamless low-alloy steel pipe with a wall thickness of 20 mm or more, having a tensile strength of 950 MPa or more, a yield strength of 850 MPa or more, and Charpy absorbed energy at −40° C. of 60 J or more, comprising:
providing a low-alloy steel having the alloy composition according to any one of claims 1 , 2 , 3 or 4 ,
hot working the low alloy steel into a steel pipe having a diameter and a wall thickness of 20 mm or more at a high temperature, and then
heating the steel pipe with said diameter and wall thickness from room temperature to a temperature of not lower than the Ac 3 transformation point, and
quenching the heated steel pipe, and
tempering the quenched steel pipe at a temperature of not higher than the Ac 1 transformation point.