Lightweight plasterboard and plaster slurry composition used for its manufacture
View Patent ↗A plaster slurry composition includes plaster, water and starch, the starch having a Brookfield viscosity of less than 60 cps at a temperature below 60° C. and a Brookfield viscosity greater than 10,000 cps at a temperature of 70° C.
1. A method for increasing the compressive strength of a plasterboard, the method comprising forming a plaster composition comprising a starch having a Brookfield viscosity of less than 60 cps at a temperature below 60° C. and a Brookfield viscosity greater than 10,000 cps at a temperature of 70° C.
2. The method according to claim 1 , wherein the compressive strength of the plasterboard is increased by at least 0.5 MPa.
3. The method according to claim 1 , wherein the starch has a Brookfield viscosity of less than 20 cps at a temperature of 60° C.
4. The method according to claim 1 , wherein the starch has a Brookfield viscosity of greater than 20,000 cps at a temperature of 70° C.
5. The method according to claim 1 , wherein the starch has a Brookfield viscosity of greater than 30,000 cps at a temperature of 70° C.
6. The method according to claim 1 , wherein the starch has a Brookfield viscosity of greater than 60,000 cps at a temperature of 80° C.
7. The method according to claim 1 , wherein the starch is non-retrograding.
8. The method according to claim 1 , wherein the starch has a viscosity at 25° C., after cooling following heating of the starch solution up to 90° C., which is greater than the maximum viscosity obtained during heating of said starch solution.
9. The method according to claim 1 , wherein the starch has a viscosity at 25° C., after cooling following heating of the starch solution up to 90° C., of at least 100,000 cps.
10. The method according to claim 1 , wherein the starch has a viscosity at 25° C., after cooling following heating of the starch solution up to 90° C., of at least 300,000 cps.