Sintered compact
View Patent ↗A sintered cubic boron nitride (cBN) compact for use in a tool is obtained by sintering a mixture of (i) cubic boron nitride, (ii) aluminum oxide, (iii) one or more refractory metal compounds, and (iv) aluminum and/or one or more non-oxide aluminum compounds. The sintered bodies may have sufficient strength and toughness to be used as a tool material in solid, i.e. not carbide supported, form, and may be useful in heavy machining of cast irons.
1. A process for making a sintered compact with a cubic boron nitride (cBN) portion and a non cBN portion, which comprises:
(A) preparing a mixture comprising:
(a) between about 71 and about 93 volume-% cBN;
(b) between about 1 and about 20 volume-% of aluminum oxide;
(c) between about 3 and about 26 volume-% of one or more refractory metal compounds selected from:
i. a compound having the general formula MZ (1-x) ;
ii. a compound having the general formula MC (1-x) N x ; and
iii. a combination or solid solutions of two or more compounds each having the general formula MZ or MZ 2 , wherein:
Z is selected from the group consisting of C, B, N and a combination thereof, M is a metal from groups IV-VI of the periodic table, and x is a number between 0.01 and 0.99; and
(d) between greater than 6 and about 20 volume-% of a source of one or more non-oxide aluminum compounds;
wherein the total aluminum content in the non cBN portion of the sintered compact exceeds about 30 weight;
wherein the cBN has a grain size distribution that is at least bimodal having a coarse portion comprising about 40% to about 80% of the cBN and a fine portion comprising about 20 to about 60% of the cBN;
wherein the coarse portion has an average grain size of about 5 to about 30 μm and the fine portion has an average grain size of about 0 to about 10 μm; and
wherein the ratio of the average grain size of the coarse portion to the average grain size of the fine portion is about 3:1 or greater; and
(B) subjecting the mixture to high pressure and high temperature (HP/HT) conditions to produce a sintered compact.
2. The process of claim 1 , wherein said HP/HT conditions include a pressure of between about 25 and about 75 kbars, and a temperature of about 1000° C. or higher.
3. The process of claim 1 , wherein the cBN has a grain size distribution that is bimodal or multimodal.
4. The process of claim 3 , wherein the ratio of the average grain size of the coarse portion to the average grain size of the fine portion is about 2:1.
5. The process of claim 1 , further comprising placing a foil or other solid form of aluminum in contact with the powder mixture during sintering.
6. A process for making a sintered compact with a cubic boron nitride (cBN) portion and a non cBN portion comprising:
(A) preparing a mixture comprising:
(a) between about 50 and about 93 weight-% of cBN with a bimodal or multimodal grain size distribution;
(b) between about 1 and about 30 weight-% of aluminum oxide;
(c) between about 3 and about 46 weight-% of one or more compounds selected from the group consisting of carbides, nitrides, borides, and carbonitrides, all of Groups IV-VI of the periodic table; and
(d) between greater than 6 and about 20 volume-% of a source of one or more non-oxide aluminum compounds;
wherein the total aluminum content in the non cBN portion of the sintered compact exceeds about 30 weight;
wherein the cBN has a grain size distribution that is at least bimodal having a coarse portion comprising about 40% to about 80% of the cBN and a fine portion comprising about 20 to about 60% of the cBN;
wherein the coarse portion has an average grain size of about 5 to about 30 μm and the fine portion has an average grain size of about 0 to about 10 μm; and
wherein the ratio of the average grain size of the coarse portion to the average grain size of the fine portion is about 3:1 or greater; and
(B) subjecting the mixture to high pressure and high temperature (HP/HT) conditions to produce a sintered compact.
7. The process of claim 6 , wherein the HP/HT conditions include a pressure of between about 25 and about 75 kbars, and a temperature of about 1000° C. or more.
8. The process of claim 6 , wherein the one or more compounds selected from the group consisting of carbides, nitrides, borides, and carbonitrides, comprise carbonitrides of the formula TiC (1-x) N x , or a mixture of at least two materials selected from the group of TiC, TiN, TiB 2 , TiN (1-x) and TiC (1-x) N x , wherein x is any value between 0.01 and 0.99.
9. The process of claim 6 , wherein the ratio of the average grain size of the coarse portion to the average grain size of the fine portion is about 2:1.
10. The process of claim 6 , further comprising placing a foil or other solid form of aluminum placed in contact with the powder mixture during high pressure and high temperature sintering.