Golf ball
A golf ball 2 includes a spherical core 4 , a mid layer 6 , and a cover 8 . The core 4 is obtained by crosslinking a rubber composition. The difference between: a hardness H(5.0) at a point which is located at a distance of 5 mm from the central point of the core 4 ; and a hardness Ho at the central point is 6.0 or greater. The difference between: a hardness H(12.5) at a point which is located at a distance of 12.5 mm from the central point; and the hardness H(5.0) is 4.0 or less. The difference between a hardness Hs at the surface of the core 4 and the hardness H(12.5) is 10.0 or greater. The difference between the hardness Hs and the hardness Ho is 22.0 or greater. There is no zone in which a hardness decreases from the central point to the surface. A Shore D hardness H3 of the cover is greater than a Shore D hardness H2 of the mid layer.
1. A golf ball comprising
a core formed by crosslinking a rubber composition including a base rubber and from 0.05 parts by weight to 3.0 parts by weight of 2-naphthalenethiol based upon 100 parts by weight of said base rubber,
a mid layer positioned outside the core, and
a cover positioned outside the mid layer,
wherein
a difference between: a JIS-C hardness H(5.0) at a point which is located at a distance of 5 mm from a central point of the core; and a JIS-C hardness Ho at the central point is equal to or greater than 6.0,
a difference between: a JIS-C hardness H(12.5) at a point which is located at a distance of 12.5 mm from the central point; and the JIS-C hardness H(5.0) is equal to or less than 3.0,
a difference between a JIS-C hardness Hs at a surface of the core and the JIS-C hardness H(12.5) is equal to or greater than 10.0,
the JIS-C hardness H(12.5) is smaller than the average value of the JIS-C hardness H(10) at a point which is located at a distance of 10.0 mm from the central point of the core and the JIS-C hardness H(15) at a point which is located at a distance of 15.0 mm from the central point of the core,
a difference between the JIS-C hardness Hs and the JIS-C hardness Ho is equal to or greater than 22.0,
a difference between the JIS-C hardness H(5.0) and the JIS-C hardness Ho is smaller than a difference between the JIS-C hardness Hs and the JIS-C hardness H(12.5), wherein a difference between the JIS-C hardness H(12.5) and the JIS-C hardness H(5.0) is equal to or less than 1.5, and a difference between the JIS-C hardness Hs and the JIS-C hardness H(12.5) is equal to or greater than 13.0, there is no zone in which a hardness decreases from the central point toward the surface,
the mid layer is constituted with a resin composition, and the base polymer of the mid layer include an ionomer resin as a principal component, and
a Shore D hardness H3 of the cover is greater than a Shore D hardness H2 of the mid layer.
2. The golf ball according to claim 1 , wherein a specific gravity SG2 of the mid layer is greater than a specific gravity SG1 of the core.
3. The golf ball according to claim 2 , wherein a difference (SG2−SG1) between the specific gravity SG2 of the mid layer and the specific gravity SG1 of the core is equal to or greater than 0.05 but equal to or less than 0.4.
4. The golf ball according to claim 1 , wherein the JIS-C hardness Ho is equal to or greater than 40.0 but equal to or less than 70.0, and the JIS-C hardness Hs is equal to or greater than 78.0 but equal to or less than 95.0.
5. The golf ball according to claim 1 , wherein a thickness of the mid layer is equal to or greater than 0.5 mm but equal to or less than 1.2 mm, and a thickness of the cover is equal to or greater than 0.3 mm but equal to or less than 1.3 mm.
6. The golf ball according to claim 1 , wherein a sum (W2+W3) of a weight W2 of the mid layer and a weight W3 of the cover is 8.4 g or greater but equal to or less than 12.0 g, and a sum (V2+V3) of a volume V2 of the mid layer and a volume V3 of the cover is equal to or less than 10 cm 3 .
7. The golf ball according to claim 1 , wherein the specific gravity SG2 of the mid layer is equal to or greater than 1.15.
8. The golf ball according to claim 1 , wherein
the cover is constituted with resin composition, and
the base polymer of the mid layer includes an ionomer resin as a principal component.
9. The golf ball according to claim 1 , wherein the JIS-C hardness H(5.0) is equal to or greater than 62.0 but equal to or less than 72.0.
10. The golf ball according to claim 1 , wherein the JIS-C hardness H(12.5) is equal to or greater than 63.0 but equal to or less than 73.0.
11. The golf ball according to claim 1 , wherein the hardness Shore D H2 is equal to or greater than 35 but equal to or less than 57.
12. The golf ball according to claim 1 , wherein the Shore D hardness H3 is equal to or greater than 57 but equal to or less than 66.
13. The golf ball according to claim 1 , wherein a difference (H3−H2) between the Shore D hardness H3 and the Shore D hardness H2 is equal to or greater than 4 but equal to or less than 20.
14. The golf ball according to claim 1 , wherein an amount of 2-naphthalenethiol is equal to or greater than 0.2 parts by weight but equal to or less than 2.0 parts by weight per 100 parts by weight of the base rubber.