1. A multilayer blown film comprising:

(a) a core layer having a first side and a second side, the core layer comprising an ethylene polymer;

(b) an inner layer positioned on the first side of the core layer, the inner layer comprising a first conjugated diene monovinylarene block copolymer; and

(c) an outer layer positioned on the second side of the core layer, the outer layer comprising a second conjugated diene monovinylarene block copolymer;

wherein:

the multilayer blown film has a MD shrink greater than about 60% and a CD shrink in a range from 0% to about 15% at 150° C.;

the multilayer blown film is not a tenter frame, double bubble, or machine direction oriented film; and

the ethylene polymer is characterized by:

a MI in a range from about 0.01 to about 2 g/10 min;

a ratio of HLMI/MI in a range from about 50 to about 300; and

a ratio of Mw/Mn in a range from about 5 to about 30.

2. The multilayer blown film of claim 1 , wherein the core layer comprises an ethylene/α-olefin polymer having a density in a range from about 0.90 to about 0.93 g/cm 3 .

3. The multilayer blown film of claim 1 , wherein the ethylene polymer is characterized by:

a MI in a range from about 0.1 to about 0.5 g/10 min;

a ratio of HLMI/MI in a range from about 60 to about 140;

a Mw in a range from about 75,000 to about 500,000 g/mol;

a ratio of Mw/Mn in a range from about 7 to about 15;

a density in a range from about 0.88 to about 0.94 g/cm 3 ;

or any combination thereof.

4. The multilayer blown film of claim 1 , wherein:

the inner layer comprises a first coupled multimodal conjugated diene monovinylarene block copolymer;

the outer layer comprises a second coupled multimodal conjugated diene monovinylarene block copolymer;

or both.

5. The multilayer blown film of claim 1 , wherein the first conjugated diene monovinylarene block copolymer and the second conjugated diene monovinylarene block copolymer each comprise at least three consecutive conjugated diene/monovinylarene mixed blocks.

6. The multilayer blown film of claim 1 , wherein the multilayer blown film has a MD:CD shrink ratio in a range from about 4:1 to about 30:1 at 150° C.

7. The multilayer blown film of claim 1 , wherein:

the inner layer comprises a first styrene/butadiene block copolymer;

the outer layer comprises a second styrene/butadiene block copolymer;

or both.

8. The multilayer blown film of claim 1 , wherein:

the inner layer comprises further comprises a general purpose polystyrene, a high impact polystyrene, a cyclic olefin copolymer, a styrene isoprene styrene copolymer, a styrene ethylene-butylene styrene polymer, or any combination thereof;

the outer layer comprises further comprises a general purpose polystyrene, a high impact polystyrene, a cyclic olefin copolymer, a styrene isoprene styrene copolymer, a styrene ethylene-butylene styrene polymer, or any combination thereof;

or both.

9. The multilayer blown film of claim 1 , wherein the multilayer blown film further comprises an additive selected from an antioxidant, an acid scavenger, an antiblock additive, a slip additive, a colorant, a filler, a polymer processing aid, a UV inhibitor, or any combination thereof.

10. The multilayer blown film of claim 1 , wherein the multilayer blown film does not comprise a tie layer between the inner layer and the core layer or between the outer layer and the core layer.

11. The multilayer blown film of claim 1 , wherein the inner layer is adjacent the first side of the core layer, and the outer layer is adjacent the second side of the core layer.

12. The multilayer blown film of claim 1 , wherein the first conjugated diene monovinylarene block copolymer and the second conjugated diene monovinylarene block copolymer comprise the same polymer.

13. The multilayer blown film of claim 1 , wherein the inner layer and the outer layer comprise the same polymer or blend of polymers.

14. The multilayer blown film of claim 1 , wherein the inner layer and the outer layer comprise different polymers or blends of polymers.

15. A label comprising the multilayer blown film of claim 1 .

16. An article comprising a container or a package and the label of claim 15 .

17. A multilayer blown film comprising:

(a) a core layer having a first side and a second side, the core layer comprising an ethylene/α-olefin polymer; and

(b) an inner layer positioned on the first side of the core layer, the inner layer comprising a first conjugated diene monovinylarene block copolymer; and

(c) an outer layer positioned on the second side of the core layer, the outer layer comprising a second conjugated diene monovinylarene block copolymer;

wherein:

the multilayer blown film has a MD shrink greater than about 60% and a CD shrink in a range from 0% to about 15% at 150° C.;

the multilayer blown film has an average film thickness in a range from about 0.5 to about 10 mils;

the multilayer blown film is not a tenter frame, double bubble, or machine direction oriented film; and

the ethylene/α-olefin polymer is characterized by:

a MI in a range from about 0.01 to about 2 g/10 min;

a ratio of HLMI/MI in a range from about 50 to about 300; and

a ratio of Mw/Mn in a range from about 5 to about 30.

18. The multilayer blown film of claim 17 , wherein:

the inner layer comprises a first styrene/butadiene block copolymer; and

the outer layer comprises a second styrene/butadiene block copolymer.

19. The multilayer blown film of claim 18 , wherein the ethylene/α-olefin polymer is characterized by:

a ratio of HLMI/MI in a range from about 50 to about 150; and

a density in a range from about 0.88 to about 0.94 g/cm 3 .

20. A label comprising the multilayer blown film of claim 19 .

21. An article comprising a container or a package and the label of claim 20 .

22. The multilayer blown film of claim 17 , wherein the multilayer blown film further comprises an additive selected from an antioxidant, an acid scavenger, an antiblock additive, a slip additive, a colorant, a filler, a polymer processing aid, a UV inhibitor, or any combination thereof.

23. The multilayer blown film of claim 17 , wherein:

the inner layer comprises a first styrene/butadiene block copolymer, and further comprises a general purpose polystyrene, a high impact polystyrene, a cyclic olefin copolymer, a styrene isoprene styrene copolymer, a styrene ethylene-butylene styrene polymer, or any combination thereof; and

the outer layer comprises a second styrene/butadiene block copolymer, and further comprises a general purpose polystyrene, a high impact polystyrene, a cyclic olefin copolymer, a styrene isoprene styrene copolymer, a styrene ethylene-butylene styrene polymer, or any combination thereof.

24. The multilayer blown film of claim 17 , wherein the multilayer blown film has a MD:CD shrink ratio in a range from about 4:1 to about 30:1 at 150° C.

25. The multilayer blown film of claim 24 , wherein the multilayer blown film has a MD shrink in a range from about 65% to about 90% at 150° C.

26. The multilayer blown film of claim 17 , wherein the multilayer blown film has:

a MD shrink in range from about 65% to about 90%;

a CD shrink in a range from 1% to about 10%;

an average film thickness in a range from about 0.5 to about 5 mils;

a haze of less than about 10%;

a 60° gloss of greater than about 100%; and

a 1% MD secant modulus greater than about 50,000 psi.

27. The multilayer blown film of claim 17 , wherein the ethylene/α-olefin polymer is characterized by:

a MI in a range from about 0.05 to about 1 g/10 min;

a ratio of HLMI/MI in a range from about 60 to about 140;

a Mw in a range from about 75,000 to about 500,000 g/mol;

a ratio of Mw/Mn in a range from about 7 to about 15; and

a density in a range from about 0.90 to about 0.93 g/cm 3 .

28. A label comprising the multilayer blown film of claim 27 .

29. The multilayer blown film of claim 17 , wherein the inner layer is adjacent the first side of the core layer, and the outer layer is adjacent the second side of the core layer.