LIGHTWEIGHT POLYPROPYLENE NETS MANUFACTURED WITH A BETA NUCLEATION ADDITIVE, THE METHOD OF MANUFACTURING AND USES THEREOF
Integral polypropylene oriented nets are made by stretching and orienting a polypropylene starting sheet material having a defined pattern of holes or depressions in which the polypropylene is at least 20%, and preferably up to about 80%, beta crystals caused by adding a beta nucleating agent to the polypropylene, preferably in concentrations between about 10 ppm to about 100 ppm. Such beta nucleated polypropylene nets exhibit increased yield and break tensile strengths, flexural stiffness, modulus characteristics, and crimping retention and resiliency over substantially identical oriented nets made from polypropylene without a beta nucleating agent added. A method for manufacturing the beta nucleated polypropylene oriented net is disclosed, along with a crimped beta nucleated polypropylene oriented net ( 16 ) and a sandwich mat product ( 10 ) for erosion control which includes the crimped beta nucleated polypropylene oriented net ( 16 ) as a layer therein.
1 . An integral biaxially oriented polypropylene net, characterized in that said polypropylene net has a minium of 20% polypropylene in the beta crystalline form.
2 . The integral polypropylene net of claim 1 , characterized in that said polypropylene net has a minimum of 50% polypropylene in the beta crystalline form.
3 . The integral polypropylene net of claim 1 , characterized in that said polypropylene net has a concentration of a beta nucleant of about 10 ppm to about 100 ppm of said net.
4 . The integral polypropylene net of claim 1 , characterized in that said polypropylene net has a least 80% polypropylene in the beta crystalline form.
5 . A method of making an integral polypropylene net by forming or casting polypropylene into a sheet like starting material having a defined pattern of holes or depressions and biaxially stretching said starting material to form a biaxially oriented net, characterized in that a beta nucleating agent is added to said polypropylene.
6 . The method of claim 5 , characterized in that said beta nucleating agent is a red quinacridone dye.
7 . The method of claim 5 , characterized in that said beta nucleating agent is present at a concentration of about 10 ppm to about 100 ppm.
8 . The method of claim 5 , characterized in that the beta nucleating agent is added in a concentrated form having about 450 ppm to about 2000 ppm of the beta nucleating agent in a polypropylene resin mixture.
9 . The integral polymer net of claim 1 , characterized in that said polypropylene net has increased tensile, torsional and flexural strength and crimping characteristics when compared to the same polypropylene net manufactured without addition of a beta nucleating agent.
10 . A crimped biaxially oriented polypropylene net, characterized in that said polypropylene net has a minium of 20%, and preferably at least 80%, polypropylene in the beta crystalline form.
11 . The integral polymer net of claim 1 , characterized in that said polypropylene net has a concentration of a beta nucleant of about 10 ppm to about 100 ppm of said net.
12 . A sandwich mat product for erosion control, characterized in that it includes as a layer the integral polymer grid of claim 10 .
13 . A sandwich mat product having an oriented polypropylene net upper layer and an oriented polypropylene net lower layer, which have sandwiched therebetween a fiber matrix material layer and a crimped polypropylene oriented net layer, characterized in that said crimped polypropylene net layer has a minimum of 20%, and preferable at least 80%, polypropylene in the beta crystalline form.
14 . The integral polymer net of claim 3 , characterized in that said beta nucleant is a red quinacridone dye.
15 . The sandwich mat product of claim 13 , characterized in that said crimped polypropylene oriented net layer has a concentration of beta nucleant of about 10 ppm to about 100 ppm of said net layer.