Applying polyester onto metal substrate

1. Processing steps for laminating a metal substrate with a thin thermoplastic polymer film to create desirable simultaneous commercial properties comprising:

a. uncoiling a metal substrate from a coil on a processing line,

b. wherein said metal substrate is flat rolled,

c. increasing the surface energy of a first major side of said metal substrate to a dyne/cm level of at least 45,

d. preheating said metal substrate to at least 200° F.,

e. preselecting a first film for bonding to said first major side, wherein said first film is either solid or molten,

f. pressing said first film onto said first major side by use of a first roll,

g. utilizing a first chemical bond for adhering said first film to said first major side thereby creating a metal polymer laminate,

h. wherein said first film comprises at least 50% thermoplastic polyester by weight,

i. wherein said polyester is PET, PBT, or a mixture of PET and PBT,

j. wherein said first film is a maximum of 0.003 inches thick,

k. wherein said first film comprises at least one layer,

l. post treating said metal polymer laminate by heating said metal polymer laminate to at least the lowest melting point of any polymer in said first film, and

m. cooling said metal polymer laminate to below 150° F. for coiling into a finished coil,

n. wherein said cooling of said metal polymer laminate creates crystallinity in said first film according to a predetermined criterion, and

whereby said finished coil has said desirable simultaneous commercial properties comprising:

o. coating continuity of at least three metal thickness bending radius without metal exposure,

p. bonding of said first film onto said metal substrate of at least 43 ounces per inch after said cooling,

q. a minimum pencil hardness of 2B.

2. The processing steps according to claim 1 wherein the following steps are optionally done prior to said post treating of said metal polymer laminate:

r. additionally heating said metal polymer laminate to at least 200° F. if necessary,

s. increasing the surface energy of the second major side of said metal substrate to a dyne/cm level of at least 45,

t. preselecting a second film for bonding to the second major side of said metal substrate,

r. pressing said second film onto the second major side by use of a second roll, wherein said second film is either solid or molten,

u. wherein said second roll is

i. opposite of said first roll to create a roll nip, or

ii. a selected distance sequentially after said first roll,

v. utilizing a second chemical bond for adhering said second film to the second major side,

w. wherein said second film comprises at least one layer, and

x. wherein said second film is a maximum of 0.003 inches thick.

3. The processing steps according to claim 2 wherein any said film is trimmed to substantially match the width of said metal substrate prior to being pressed against said metal substrate.

4. The processing steps according to claim 2 wherein the crystallinity of any said polyester is maximized by timing said cooling of polymer metal laminate.

5. The processing steps according to claim 2 wherein any said chemical bond is created by use of an anhydride, acrylic acid, glycol, or an acrylate molecular group.

6. The processing steps according to claim 2 wherein at least one of the group comprising i) said first roll and ii) said second roll is heated to a controlled temperature.

7. The processing steps according to claim 2 wherein said processing line includes strip storage to allow coils to be spliced together inline.

8. The processing steps according to claim 2 wherein any said preheating or post heating is automatically regulated based on the lengthwise speed of said metal substrate on said processing line and includes any efficiency effects that vary with the lengthwise speed of said metal substrate on said processing line.

9. The processing steps according to claim 2 wherein said chemical bond is created by use of a PETG tie layer, and said cooling provides a pencil hardness of a minimum of 5H.