Dry-coated oxygen-scavenging particles and methods of making them
View Patent ↗A method of dry coating oxidizable particles with activating particles. The method includes accreting at least portions of the activating particles onto surfaces of the oxidizable particles by mechanically induced juxtapositions to form composite particles; and abrading the composite particles to more evenly distribute the activating component over surfaces of the activating particles.
1. A batch of composite oxygen-scavenging particles that react with oxygen in the presence of liquid phase water or water vapor, comprising:
(a) oxidizable component particles being dry coated with activating component particles by mechanical force forming composite particles; and
(b) the composite particles being mechanically abraded while continuing to be dry coated by mechanical forces for reducing irregularities within the activating component coating wherein said activating component particles comprises halide.
2. The batch of claim 1 in which the oxidizable component particles are made of an oxidizable metal or an alloy of such metals.
3. The batch of claim 2 in which the oxidizable metal or an alloy of such metals selected from the group consisting of iron, aluminum, copper, zinc, manganese, and magnesium.
4. The batch of claim 2 in which the activating component particles include at least one of electrolytic component particles, acidifying component particles, and protic solvent hydrolyzable component particles.
5. The batch of claim 2 in which the activating component particles are formed from at least one of, metal halide, a protic solvent hydrolyzable halogen compound, a sulfate, a bisulfate, a hydrated metal sulfate and/or bisulfate complex, and a ferrous sulfate monohydrate.
6. The batch of claim 2 in which the activating component particles are formed from NaHSO 4 .
7. The batch of claim 1 in which the oxidizable component particles have a hardness substantially less than the activating component particles.
8. The batch of claim 2 in which the oxidizable component particles have a mean particle diameter substantially larger than a mean particle diameter of the activating component particles.
9. The batch of claim 8 in which the mean particle diameter of the oxidizable component particles is approximately five to ten times larger than the mean particle diameter of the activating component particles.
10. The batch of claim 9 in which the mean particle diameter of the oxidizable component particles is between 1 micron and 50 microns.
11. The batch of claim 9 in which the mean particle diameter of the oxidizable component particles is between 5 microns and 15 microns.
12. The batch of claim 9 in which the mean particle diameter of the activating component particles is between 0.1 microns and 5 microns.
13. The batch of claim 9 in which the mean particle diameter of the activating component particles is between 0.2 microns and 3 microns.
14. The batch of claim 2 in which the activating component particles comprise 2 percent to 15 percent by weight of the batch.
15. The batch of claim 2 in which the activating component particles comprise 4 percent to 10 percent by weight of the batch.
16. The batch of claim 2 further comprising optically masking component particles that are dry coated onto the oxidizable component particles by mechanically-induced juxtapositions for forming the composite particles that are subject to abrasion.
17. The batch of claim 2 in which the activating component particles include at least two different kinds of particles.
18. The batch of claim 17 in which one of the activating component particles is an electrolytic component particle and a second of the activating component particles is an acidifying component particle.
19. The batch of claim 18 in which a third activating component particle masks color changes accompanying oxidation of the oxidizable component particles.
20. An oxygen-scavenging masterbatch, comprising:
(a) composite oxygen-scavenging particles including oxidizable component particles dry coated with an activating component;
(b) a base polymer forming a matrix for embedding the oxygen-scavenging particles;
(c) the composite oxygen-scavenging particles being embedded within the matrix of the base polymer, together forming a plurality of solid concentrates; and
(d) the composite oxygen-scavenging particles occupying at least five percent by weight of solid concentrates; wherein the activating component comprises a halide and wherein oxidizable component particles are dry coated with the activating component in a particle form.
21. The masterbatch of claim 20 in which the composite oxygen-scavenging particles are embedded within the matrix of the base polymer by blending the composite oxygen-scavenging particles in a liquid state of the base polymer and re-solidifying the base polymer.
22. The masterbatch of claim 20 in which the base polymer is a thermoplastic resin.
23. The masterbatch of claim 21 in which the composite oxygen-scavenging particles occupy between 5 percent and 25 percent by weight of solid concentrates.
24. The masterbatch of claim 21 in which the solid concentrates have a granular form.
25. The masterbatch of claim 21 in which oxidizable component particles are dry coated with the activating component particles by mechanically-induced juxtapositions forming the composite particles.
26. The masterbatch of claim 21 in which the composite particles are mechanically abraded while being dry coated in different mechanically-induced juxtapositions for reducing irregularities within the activating component coating.
27. The masterbatch of claim 26 in which the oxidizable component particles are made of an oxidizable metal or an alloy of such metals.
28. The masterbatch of claim 21 in which the activating component particles include at least one of electrolytic component particles, acidifying component particles, and protic solvent hydrolyzable component particles.
29. The masterbatch of claim 21 in which the oxidizable component particles and the activating component particles have substantially different hardnesses.
30. The masterbatch of claim 21 in which the oxidizable component particles have a mean particle diameter substantially larger than a mean particle diameter of the activating component particles.
31. The masterbatch of claim 21 in which the activating component particles comprise 2 percent to 15 percent by weight of the composite oxygen-scavenging particles.
32. The masterbatch of claim 31 wherein the activating component particles comprise component particles that mask color changes accompanying oxidation of the oxidizable component particles.