Injection molded article and method for the manufacture thereof
View Patent ↗Articles injection molded from colored poly(arylene ether) compositions can exhibit an esthetic defect known as black rings. The black rings can be reduced or eliminated when the poly(arylene ether) composition includes about 50 to about 70 weight percent of a poly(arylene ether), about 12 to about 30 weight percent of a rubber-modified polystyrene, about 5 to about 25 weight percent of an organophosphate ester flame retardant, and a first colorant and a second colorant, wherein the total amount of all colorants is about 0.3 to about 1 weight percent.
1. A method of reducing esthetic defects in an injection molded article, the method comprising:
injection molding a poly(arylene ether) composition to form an injection molded article;
wherein a portion of the injection molded article comprises
a first dimension of at least 10 centimeters,
a second dimension of at least 10 centimeters, and
a third dimension of less than or equal to 1 centimeter;
wherein the poly(arylene ether) composition comprises
about 50 to about 70 weight percent of a poly(arylene ether) having an intrinsic viscosity of about 0.3 to about 0.55 deciliter/gram measured at 25° C. in chloroform,
about 12 to about 30 weight percent of a rubber-modified polystyrene,
wherein the rubber-modified polystyrene comprises polystyrene and polybutadiene,
about 5 to about 25 weight percent of an organophosphate ester flame retardant,
a first colorant and a second colorant, wherein the total amount of all colorants is about 0.3 to about 1 weight percent, and
about 1 to about 5 weight percent of a hydrocarbon resin selected from the group consisting of aliphatic/aromatic hydrocarbon resins, hydrogenated aliphatic/aromatic hydrocarbon resins, cycloaliphatic hydrocarbon resins, hydrogenated cycloaliphatic hydrocarbon resins, cycloaliphatic/aromatic hydrocarbon resins, hydrogenated cycloaliphatic/aromatic hydrocarbon resins, hydrogenated aromatic hydrocarbon resins, polyterpene resins, terpene-phenol resins, rosins, hydrogenated rosins, rosin esters, hydrogenated rosin esters, coumarone/indene resins, hydrogenated terpene resins, and combinations thereof;
wherein all weight percents are based on the total weight of the poly(arylene ether) composition.
2. The method of claim 1 , wherein the first colorant comprises a white pigment and the second colorant comprises a black pigment.
3. The method of claim 1 , wherein the first colorant comprises about 0.25 to about 1.0 weight percent of a white pigment, and the second colorant comprises about 0.04 to about 0.1 weight percent of a carbon black.
4. The method of claim 1 , wherein the poly(arylene ether) composition comprises less than or equal to 0.2 weight percent of a poly(ethylene oxide)-poly(propylene oxide) block copolymer.
5. The method of claim 1 , wherein the poly(arylene ether) composition further comprises about 0.025 to about 0.4 weight percent of a poly(styrene-acrylonitrile)-encapsulated polytetrafluoroethylene.
6. The method of claim 1 , wherein the poly(arylene ether) composition further comprises about 0.5 to about 4 weight percent of an ethylene homopolymer.
7. The method of claim 1 , wherein the poly(arylene ether) composition further comprises about 1 to about 4 weight percent of a hydrogenated block copolymer of an alkenyl aromatic compound and a conjugated diene.
8. The method of claim 1 , wherein said injection molding comprises using an injection molding machine with a barrel temperature of about 270 to about 310° C. and a mold temperature of about 45 to about 70° C.
9. The method of claim 1 , wherein the injection molded article is a case for a lead-acid battery.
10. The method of claim 1 , wherein a surface of the injection molded article exhibits CIE 1976 L*a*b* parameters L* of about 25 to about 45, a* of −10 to about 10, and b* of −10 to about 10, determined according to ASTM D2244-09b.
11. The method of claim 1 ,
wherein the first colorant comprises about 0.25 to about 1.0 weight percent of a white pigment, and the second colorant comprises about 0.04 to about 0.1 weight percent of a carbon black;
wherein the poly(arylene ether) composition comprises less than or equal to 0.2 weight percent of a poly(ethylene oxide)-polypropylene oxide) block copolymer;
wherein the poly(arylene ether) composition further comprises about 0.025 to about 0.4 weight percent of a poly(styrene-acrylonitrile)-encapsulated polytetrafluoroethylene;
wherein the poly(arylene ether) composition further comprises about 0.5 to about 4 weight percent of an ethylene homopolymer;
wherein the poly(arylene ether) composition further comprises about 1 to about 4 weight percent of a hydrogenated block copolymer of an alkenyl aromatic compound and a conjugated diene;
wherein said injection molding comprises using an injection molding machine with a barrel temperature of about 270 to about 310° C. and a mold temperature of about 45 to about 70° C.; and
wherein the injection molded article is a case for a lead-acid battery.
12. An injection molded article formed by the method of claim 1 .
13. The injection molded article of claim 12 , wherein the injection molded article is a case for a lead-acid battery.
14. The method of claim 1 , wherein the hydrocarbon resin is selected from the group consisting of hydrogenated cycloaliphatic hydrocarbon resins, hydrogenated terpene resins, and combinations thereof.