Low-permeation flexible fuel hose
View Patent ↗A flexible hose or a tubing having a barrier layer of polyamide 6 having an impact modifier, and/or branched molecular structure, a flexural modulus of 1 to 2 GPa and/or a tensile elongation of 100% or more. The hose may have additional layers such as an HNBR rubber inner tube, an EVM/CPE rubber blend outer cover, a textile or wire reinforcement, or the like. Permeability to ethanol- and methanol-containing fuels is very low. Permeability to B20 biofuels is very low.
1. A fuel hose suitable for biofuel or alcohol-containing fuel comprising:
an HNBR rubber inner tube wherein said HNBR rubber is zinc free;
a rubber outer cover based on an elastomer blend consisting of EVM and CPE;
an intermediate barrier layer consisting essentially of an impact-modified polyamide 6 wherein the radial thickness of said barrier layer is in the range of from 0.025 mm to 0.76 mm; and
a textile reinforcement disposed between said barrier layer and said outer cover.
2. The fuel hose of claim 1 wherein said polyamide 6 has branched molecular structure.
3. The fuel hose of claim 1 wherein the polyamide 6 has a flexural modulus of from 1 to 2 GPa.
4. The fuel hose of claim 3 wherein the polyamide 6 has a tensile elongation at break of about 100% or more.
5. The fuel hose of claim 1 comprising only non-fluoropolymer-based layers.
6. The fuel hose of claim 1 wherein said barrier layer is a seamless, tubular layer.
7. The fuel hose of claim 1 further comprising an elastomeric tie layer between said barrier layer and at least one of said rubber tube and rubber cover layers.
8. The fuel hose of claim 1 wherein said barrier layer is a seamless, tubular layer.
9. The fuel hose of claim 8 wherein said polyamide 6 exhibits the following physical properties:
Tensile modulus according to ISO 527 type 1A of about 1850/1000 MPa;
Tensile strength at yield according to ISO 527 type 1A of about 55/45 MPa;
Tensile strain at break according to ISO 527 type 1A of about 150/220%;
Flexural modulus according to ISO 178 of about 1750/850 MPa;
Flexural maximum stress according to ISO 178 of about 70/45 MPa; and
Either Charpy notched impact strength according to ISO 179/1eA of about 92/NB kJ/m2, wherein NB signifies No Break, or
Izod notched impact strength according to ISO 180/1A of about 90/NB kJ/m2, wherein NB signifies No Break;
wherein if two values are listed, the first is for Dry As Molded material, and the second value is for material conditioned according ISO 1110.
10. A hose comprising:
an HNBR rubber inner tube wherein said HNBR rubber is zinc free;
an EVM/CPE blend rubber outer cover;
an intermediate barrier layer consisting essentially of an impact-modified polyamide 6 wherein the radial thickness of said barrier layer is in the range of from 0.025 mm to 0.76 mm; and
a textile reinforcement disposed between said barrier layer and said outer cover.
11. The hose of claim 10 further comprising an HNBR rubber tie layer disposed between said barrier layer and said reinforcement.
12. The hose of claim 10 further comprising an EVM/CPE blend rubber tie layer between said barrier layer and said reinforcement.
13. The hose of claim 10 wherein the textile reinforcement comprises aramid fibers.
14. The hose of claim 10 wherein the polyamide 6 has branched molecular structure.
15. The hose of claim 10 wherein said polyamide 6 has a flexural modulus of from about 1 to about 2 GPa and a tensile elongation at break of 100% or more.
16. The hose of claim 10 having at least one of a permeability to gasoline of about 1 g/m 2 /day or less at 40° C. and a permeability to B20 biofuel of less than 1 g/m 2 /day at 40° C. when tested according to SAE J1737.
17. A hose system comprising:
at least one length of hose according to claim 10 and
at least one fitting, clamp, or fluid-handling device.
18. The hose system of claim 17 wherein said polyamide 6 exhibits the physical properties, mechanical properties, and thermal properties:
Water absorption according to ISO 62 tested 24 h at 23° C. of about 1.20%;
Density according to ISO 1183-A of about 1.05 g/cc;
Tensile modulus according to ISO 527 type 1A of about 1850/1000 MPa;
Tensile strength at yield according to ISO 527 type 1A of about 55/45 MPa;
Tensile strain at break according to ISO 527 type 1A of about 150/220%;
Flexural modulus according to ISO 178 of about 1750/850 MPa;
Flexural maximum stress according to ISO 178 of about 70/45 MPa;
At least one impact property selected from: Charpy notched impact strength according to ISO 179/1eA of about 92/NB kJ/m2, wherein NB signifies No Break;
Charpy unnotched impact strength according to ISO 179/1eU NB/NB kJ/m2; and
Izod notched impact strength according to ISO 180/1A of about 90/NB kJ/m2;
Melting Temperature according to ISO 11357 of about 222° C.; and
Heat deflection temperature at 1.8 MPa according to ISO 75/Af of about 55° C.;
wherein if two values are listed, the first is for Dry As Molded material, and the second value is for material conditioned according ISO 1110.
19. The hose according to claim 8 wherein said polyamide 6 has branched molecular structure, a flexural modulus of from 1 to 2 GPa, and a tensile elongation at break of about 100% or more.