View Patent ↗The density of rigid foamed articles made by the thermal decomposition of a blowing agent in a vinyl chloride polymer is reduced by the use of a tin based blowing agent activator(s). The tin based activator also reduces the activation temperature of a chemical blowing agent, allowing for more optimal evolution of gas during plastic processing. Dibutyl tin oxide or tin maleates are superior activators of vinyl chloride polymer blowing agents.
1. A composition for preparing rigid cellular vinyl chloride polymers, said composition consisting of:
a. at least one vinyl chloride homopolymer or a copolymer comprising polymerized units of vinyl chloride and at least one ethylenically unsaturated monomer; and
b. at least one blowing agent, and
c. a blowing agent activator selected from the group consisting of dibutyl tin oxide; the reaction product of maleic anhydride, stearyl alcohol, water, and dibutyl tin oxide; and mixtures thereof.
2. The composition of claim 1 wherein said vinyl chloride homopolymer or vinyl chloride copolymer or mixtures thereof comprises from about 70% to about 95% by weight of said composition.
3. The composition of claim 1 wherein said blowing agent is selected from the group consisting of azobisformamide, 5-phenyl tetrazole, benzene sulfonyl hydrazide, citric acid, sodium bicarbonate and mixtures thereof.
4. The composition of claim 1 wherein said blowing agent comprises from about 0.1% to about 10.0% by weight of the composition.
5. The composition of claim 1 wherein said blowing agent activator comprises from about 0.01 wt % to about 10 wt % of said blowing agent composition.
6. The composition of claim 1 wherein the particle size of said blowing agent activator ranges from about 10 microns to about 100 microns.
7. The composition of claim 1 further consisting of from about 2 parts to about 18 parts acrylic resin per hundred parts of the vinyl chloride homopolymer or vinyl chloride copolymer or mixture thereof.
8. The composition of claim 1 wherein said blowing agent
activator comprises from about 0.1 parts to about 10 parts per 100 parts of the vinyl chloride homopolymer or vinyl chloride copolymer or mixture thereof.
9. The composition of claim 1 wherein the particle size of said blowing agent activator ranges from about 5 microns to about 500 microns.
10. The composition of claim 1 wherein the copolymer of vinyl chloride comprises at least 70% by weight of vinyl chloride based on total momoner weight.
11. The composition of claim 1 wherein the copolymer of vinyl chloride comprises from 1 to 30% of a copolymerizable ethylenically unsaturated monomer selected from the group consisting of vinyl acetate, vinyl butyrate, vinyl benzoate, vinylidene chloride, diethyl fumarate, diethyl maleate, other alkyl fumarates and maleates, vinyl propionate, methyl acrylate, 2-ethylhexyl acrylate, butyl acrylate, other alkyl acrylates, methyl methacrylate, ethyl methacrylate, butyl methacrylate, other alkyl methacrylates, methyl alpha-chloroacrylate, styrene, trichloroethylene, vinyl ethers, vinyl ketones 1-fluoro-2-chloroethylene, acrylonitrile, chloroacrylonitrile, allylidene diacetate and chloroallylidene diacetate.