Assembling titanium and steel parts by diffusion welding
View Patent ↗A method of assembling together titanium parts and steel parts by diffusion welding, the method interposing two thin layers of niobium or vanadium and copper respectively between a titanium part and a steel part, evacuating the assembly of parts and interposed metal layers, and subjecting the assembly to hot isostatic compression at a temperature lying in a range 900° C. to 950° C. and at a pressure lying in a range 1000 bars to 1500 bars for about two hours. The method can be applied to fabricating turbine shafts for turbomachines.
1. A method of assembling together titanium parts and steel parts by diffusion welding, the method comprising:
interposing two thin metal layers between a titanium part and a steel part, the two metal layers comprising a thin layer or foil of niobium or vanadium in addition to the titanium and a thin layer or foil of copper in addition to the steel;
putting an assembly comprising the two parts and the two interposed metal layers under a vacuum;
subjecting the assembly to hot isostatic compression at a temperature lying in a range 900° C. to 950° C., and at a pressure lying in a range 1000 bars to 1500 bars, the hot isostatic compression being followed by controlled cooling; and
subsequently subjecting the assembly to heat treatment during which the assembly is maintained at a pressure in a range 1000 bars to 1500 bars.
2. A method according to claim 1 , wherein a duration of the hot isostatic compression lies in a range one hour to three hours, approximately.
3. A method according to claim 1 , the heat treatment includes a first dwell at about 800° C., followed by cooling, a second dwell at about 450° C., and cooling.
4. A method according to claim 1 , wherein the interposed metals present a thickness lying in a range about 20 μm to about 50 μm.
5. A method according to claim 1 , further comprising machining ends of the parts for assembling together to give the ends of the parts non-plane complementary shapes, the end of the steel part including at least one projecting portion engaged in an indentation in the titanium part.
6. A method according to claim 5 , further comprising giving a conical or a biconical shape to the ends of the parts.
7. A method according to claim 1 , wherein the interposed metals are formed by depositing metal on the ends of the parts that are to be assembled.
8. A method according to claim 1 , further comprising stamping the interposed metals to give the interposed metals a shape corresponding to the shape of the ends of the parts.
9. A method according to claim 1 , wherein the putting the assembly under the vacuum includes placing the assembly inside a container suitable for hot isostatic compression, creating the vacuum inside the container, and closing the container such that the container is leaktight, and
wherein the subjecting the assembly to hot isostatic compression includes placing the container in a hot isostatic compression enclosure.
10. A method according to claim 9 , wherein the container is closed by welding.
11. A method according to claim 9 , wherein the container is a stainless steel container.
12. A method according to claim 9 , wherein the vacuum is created inside the container for approximately twelve hours.