Process for the production and treatment of graphite powders
The disclosure relates to processes for the production and thermal treatment of carbon material, in particular, graphite powders, in an Acheson type oven, using a functional filler comprising graphitic material in particulate form allowing electrical current to flow through the charge. The particulate form of the filler allows greater flexibility and can be used to control the degree of direct and indirect heating, resulting in more uniform products. Such graphite materials may typically be employed as an additive in polymers, batteries, or other applications.
1. A process for thermal treatment of carbonaceous material, the process including:
heating a charge including the carbonaceous material, wherein, in addition to the carbonaceous material to be treated, a functional filler comprising graphitic material in particulate form is added to form a mixture for allowing electrical current to flow through the charge, and wherein at least 5% by weight of functional filler is present in the mixture; and
separating the carbonaceous material from the functional filler following treatment of the carbonaceous material via classification.
2. The process according to claim 1 , wherein said graphitic material of the functional filler has a particle size ranging from about 10 μm to about 1 mm.
3. The process according to claim 1 , wherein the degree of direct and indirect heating of the carbonaceous material is controlled through a mutual three-dimensional arrangement of the functional filler and the carbonaceous material to be heat treated.
4. The process according to claim 1 , wherein the carbonaceous material is charged to an Acheson oven in the form of the mixture, and the mixture comprises:
a) the carbonaceous material to be treated, and
b) the functional filler comprising graphitic material in particulate form allowing electrical current to flow through the charge.
5. The process according to claim 1 , wherein the carbonaceous material is charged to an Acheson oven in the form of layers separated by one or more layers of said functional filler.
6. The process according to claim 5 , wherein the layers of carbonaceous material and the functional filler are oriented in an alternating manner when viewed in a cross-section.
7. The process according to claim 1 , wherein the carbonaceous material is charged to an Acheson oven in the form of a core bar, wherein said core bar is surrounded by the functional filler allowing electrical current flow.
8. The process according to claim 1 , wherein the carbonaceous material to be treated is charged to an Acheson oven, and wherein the graphitic material in particulate form is disposed between electrodes in the form of one or more bars.
9. The process according to claim 8 , wherein the bars of the graphitic material are of rectangular shape when viewed in a cross-section.
10. The process according to claim 1 , wherein the carbonaceous material is charged to an Acheson oven within graphitic containers, and wherein the graphitic containers are embedded into the functional filler allowing electrical current flow.
11. The process according to claim 1 , wherein the functional filler and the carbonaceous material are of different grain size, thereby allowing the separation of the treated carbonaceous particles from the functional filler particles.
12. The process according to claim 11 , wherein the content of the cold oven after the thermal treatment is classified through sieves having mesh sizes corresponding to the grain sizes of the employed filler and carbonaceous materials, respectively.
13. The process according to claim 1 , wherein the carbonaceous material and/or the functional filler further contain one or more catalyst compounds or other additives.
14. The process according to claim 1 , wherein in addition to the carbonaceous material to be treated and the functional filler, a carbonaceous material with low conductivity in particulate form is added to the reactor as a solid bulk insulator.
15. The process according to claim 14 , wherein said carbonaceous material with low conductivity is selected from petroleum coke and anthracite.
16. The process according to claim 1 , wherein the carbonaceous material to be treated is a material to be graphitized.
17. The process according to claim 1 , wherein the carbonaceous material is a graphitic material to be heat treated and/or purified.