Thermoplastic material
View Patent ↗Use of a thermoplastic material for blocking an optical substrate ( 100 ) in a machining position, wherein the thermoplastic material is formulated from a composition comprising a shellac and a plasticizer where the shellac and the plasticizer are chosen so as to have the softening point of the thermoplastic material greater than or equal to 60° C. and smaller than or equal to 85° C.
1. A method of blocking an optical substrate in a machining position, the method comprising:
heating a thermoplastic material formulated from a composition comprising a shellac and a plasticizer, wherein the shellac and the plasticizer are chosen so as to have the softening point of the thermoplastic material greater than or equal to 60° C. and less than or equal to 85° C.; and
docking the optical substrate to the thermoplastic material so as to be positioned in a machining position.
2. The method of claim 1 , wherein the shellac and plasticizer are chosen so as to have the hardness of the thermoplastic material at room temperature greater than or equal to 40 when measured using the Shore D method.
3. The method of claim 1 wherein the composition comprises, as a percentage by weight of the thermoplastic material, at least or equal to 60% and at most or equal to 80% of shellac.
4. The method of claim 1 , wherein the composition comprises, as a percentage by weight of the thermoplastic material, at least or equal to 20% and at most or equal to 40% of plasticizer.
5. The method of claim 1 wherein the shellac comprises at least one of waxed shellac, dewaxed shellac, and bleached shellac.
6. The method of claim 1 wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of rosin or modified rosin.
7. The method of claim 6 , wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of ester of rosin.
8. The method of claim 1 , wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of hydrocarbon-based resin.
9. The method of claim 1 , wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of C5 aliphatic hydrocarbon resin.
10. A preformed optical substrate block comprising a thermoplastic block used to allow an optical substrate to be blocked on the preformed optical substrate block wherein the thermoplastic block is formulated from a composition comprising a shellac and a plasticizer where the shellac and the plasticizer are chosen so as to have the softening point of the thermoplastic material greater than or equal to 60° C. and less than or equal to 85° C.
11. The preformed optical substrate block according to claim 10 , wherein the shellac and plasticizer are chosen so as to have the hardness of the thermoplastic material at room temperature greater than or equal to 40 when measured using the Shore D method.
12. The preformed optical substrate block according to claim 10 , wherein the composition comprises, as a percentage by weight of the thermoplastic material, at least or equal to 60% and at most or equal to 80% of shellac.
13. The preformed optical substrate block according to claim 10 , wherein the composition comprises, as a percentage by weight of the thermoplastic material, at least or equal to 20% and at most or equal to 40% of plasticizer.
14. The preformed optical substrate block according to claim 10 , wherein the shellac comprises at least one of waxed shellac, dewaxed shellac, and bleached shellac.
15. The preformed optical substrate block according to claim 10 , wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of rosin or modified rosin.
16. The preformed optical substrate block according to claim 15 , wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of ester of rosin.
17. The preformed optical substrate block according to claim 10 , wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of hydrocarbon-based resin.
18. The preformed optical substrate block according to claim 10 , wherein the plasticizer comprises, as a percentage by weight of the plasticizer, at least or equal to 80% of C5 aliphatic hydrocarbon resin.
19. A method of blocking an optical substrate to be machined, the method comprising the steps of:
an optical substrate providing step in which an optical substrate is provided;
a preformed optical substrate block providing step in which a preformed optical substrate block is provided, wherein:
the preformed optical substrate block comprises a thermoplastic block configured to allow an optical substrate to be blocked on the preformed optical substrate block,
the thermoplastic block is formulated from a composition comprising a shellac and a plasticizer where the shellac and the plasticizer are chosen so as to have the softening point of the thermoplastic material greater or equal to 60° C. and less than or equal to 85° C.;
a surface heating step in which a surface of the preformed substrate block is heated at a docking temperature that is 10° C. to 25° C. less than the softening temperature of the thermoplastic material; and
a docking step in which the optical substrate is docked to the heated surface of the preformed substrate block so as to be positioned in a machining position.