Multi-stage process for producing polyethylene with lowered gel formation
View Patent ↗The present inventions relates to a process for producing polyethylene compositions comprising polymerizing polyethylene resins in a cascaded multi-stage reaction in which the reaction steps are performed in at least two slurry phase reactors (A) and (B) and at least one gas phase reactor (C) which are arranged in series in any order wherein in reactor (A) a low molecular weight ethylene homo- or copolymer fraction having a MFR 2 of 100 to 2000 g/10 min, in reactor (B) a low molecular weight ethylene homo- or copolymer fraction having an MFR 2 of 100 to 2000 g/10 min, and in reactor (C) a high molecular weight ethylene copolymer fraction are polymerized, and further comprising a compounding step after polymerization, wherein the final polyethylene composition has a MFR 21 of 3 to 50 g/10 min, the melt flow rates being determined according to ISO 1133.
1. A process for producing polyethylene compositions comprising producing polyethylene resins in a cascaded multi-stage reaction in which the reaction steps are performed in at least two slurry phase polymerization reactors (A) and (B) and at least one gas phase polymerization reactor (C) which are arranged in series in any order wherein
in reactor (A) a low molecular weight ethylene homo- or copolymer fraction having a MFR 2 of 100 to 2000 g/10 min,
in reactor (B) a low molecular weight ethylene homo- or copolymer fraction having an MFR 2 of 100 to 2000 g/10 min, and
in reactor (C) a high molecular weight ethylene copolymer fraction are produced, and
further comprising a compounding step after polymerisation,
wherein the final polyethylene composition has a MFR 21 of 3 to 50 g/10 min, the melt flow rates being determined according to ISO 1133.
2. The process according to claim 1 wherein the polymerisation in at least one of slurry phase polymerization reactors (A) and (B) is carried out in the presence of an inert hydrocarbon medium is selected from the group comprising C 3 to C 8 hydrocarbons.
3. The process according to claim 1 wherein the polymerisation in at least one of slurry polymerization reactors (A) or (B) is carried out under supercritical conditions whereby the reaction temperature and reaction pressure are above respective critical points of the mixture formed by the hydrocarbon medium, monomer, hydrogen and optional comonomer and the polymerisation temperature is lower than the melting temperature of the polymer formed.
4. The process according to claim 1 wherein in reactor (A) an ethylene homo- or copolymer fraction in an amount of 10 to 30 wt % of the total polyethylene resin is produced.
5. The process according claim 1 to wherein in reactor (A) an ethylene homopolymer fraction is produced.
6. The process according to claim 1 wherein in reactor (B) an ethylene homo- or copolymer fraction in an amount of 15 to 40 wt % of the total polyethylene resin is produced.
7. The process according to claim 1 wherein in reactor (B) an ethylene homopolymer fraction is produced.
8. The process according to claim 1 wherein one or more comonomers selected from the group comprising C 4 to C 8 alpha-olefins are fed to the reaction mixture in reactor (C).
9. The process according to claim 8 wherein the comonomer is 1-hexene.
10. The process according to claim 1 wherein in reactor (C) an ethylene copolymer fraction in an amount of 30 to 75 wt % of the total polyethylene resin is produced.
11. The process according to claim 1 wherein the polymerisation conditions in reactor (C) are selected as such that the final polyethylene composition has a MFR 5 of 0.05 to 2 g/10 min, determined according to ISO 1133.
12. The process according to claim 1 wherein the polymerisation is carried out in the presence of a Ziegler-Natta catalyst.
13. A multimodal polymer composition comprising a polyethylene resin comprising
(i) a first low molecular weight ethylene homo- or copolymer fraction having a MFR 2 of 100 to 2000 g/10 min,
(ii) a second low molecular weight ethylene homo- or copolymer fraction having a MFR 2 of 100 to 2000 g/10 min, and
(iii) a high molecular weight ethylene copolymer fraction,
wherein the polyethylene resin has a MFR 21 of 3 to 50 g/10 min and white spots are dispersed within the final composition with a white spot dispersion of less than 4.5 after a single compounding step, the melt flow rates being determined according to ISO 1133 and the white spot test according to ISO 18553.
14. The polymer composition according to claim 13 wherein polyethylene fraction (i) is present in an amount of 10 to 30 wt %, polyethylene fraction (ii) is present in an amount of 15 to 45 wt %, and polyethylene fraction (iii) is present in an amount of 30 to 75 wt %, based on the total amount of the polyethylene resin.
15. The multimodal polymer composition according to claim 13 wherein combined polyethylene fractions (i) and (ii) are present in an amount of at least 53 wt % of the total polyethylene resin.
16. The multimodal polymer composition according to claim 13 wherein at least one of polyethylene fractions (i) or (ii) is an ethylene homopolymer and polyethylene fraction (iii) is an ethylene copolymer having comonomer units selected from comprising C 4 to C 8 alpha-olefins.