Negative electrode for nanaqueous electrolyte secondary battery, nonaqueous electrolyte secondary battery using the same, and method for manufacturing negative electrode for nonaqueous electrolyte secondary battery
View Patent ↗There is provided a negative electrode for a nonaqueous electrolyte secondary battery in which when a battery is formed, the energy density is high, and moreover, the decrease in charge and discharge capacity is small even if charge and discharge are repeated. By using silicon oxide particles having a particle diameter in a particular range as a starting raw material, and heating these particles in the range of 850° C. to 1050° C., Si microcrystals are deposited on the surfaces of the particles. Then, by performing doping of Li, a structure comprising a plurality of protrusions having height and cross-sectional area in a particular range is formed on the surfaces. The average value of the height of the above protrusions is 2% to 19% of the average particle diameter of the above lithium-containing silicon oxide particles. By using the lithium-containing silicon oxide particles obtained by the above means as a negative electrode active material, a negative electrode for a nonaqueous electrolyte secondary battery is fabricated.
1. A negative electrode for a nonaqueous electrolyte secondary battery comprising lithium-containing silicon oxide particles of a spherical shape, wherein the lithium-containing silicon oxide particles have a structure comprising a plurality of protrusions comprising a lithium-containing silicon oxide on a surface thereof, wherein the protrusions extend outward from the surface of the lithium-containing silicon oxide particles.
2. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 1 , comprising a conductive auxiliary agent and a binder.
3. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 1 , wherein the structure comprising a plurality of protrusions is formed on a surface of the lithium-containing silicon oxide particles by using silicon oxide particles as a starting raw material, subjecting the silicon oxide particles to heating treatment, and then performing doping and dedoping of lithium by electrochemical means.
4. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 3 , wherein an oxidation amount in the silicon oxide particles is 0.8 to 1.0 with respect to one silicon atom.
5. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 3 , wherein heating temperature in the heating treatment is 850° C. to 1050° C.
6. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 3 , wherein an average value of cross-sectional area at bottom portions of the protrusions is 0.4 μm 2 to 5.4 μm 2 .
7. The negative electrode for nonaqueous electrolyte secondary battery according to claim 3 , wherein an amount of the doping of lithium by the electrochemical means is 1.4 mol to 3.8 mol with respect to 1 mol of silicon in the silicon oxide particles.
8. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 3 , wherein an average particle diameter of the silicon oxide particles that are a starting raw material is 5 μm to 30 μm.
9. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 1 , wherein an average value of height of the protrusions is 5% to 16% of the average particle diameter of the lithium-containing silicon oxide particles.
10. A nonaqueous electrolyte secondary battery using a negative electrode for a nonaqueous electrolyte secondary battery according to claim 1 .
11. A method for manufacturing a negative electrode for a nonaqueous electrolyte secondary battery, comprising obtaining lithium-containing silicon oxide particles of a spherical shape each having a structure comprising a plurality of protrusions comprising a lithium-containing silicon oxide on a surface thereof by using silicon oxide particles as a starting raw material, subjecting the silicon oxide particles to heating treatment, and then performing doping and dedoping of lithium by electrochemical means, wherein an average value of height of the protrusions is 2% to 19% of an average particle diameter of the lithium-containing silicon oxide particles, and the protrusions extend outward from the surface of the lithium-containing silicon oxide particles.
12. The method for manufacturing a negative electrode for a nonaqueous electrolyte secondary battery according to claim 11 , comprising mixing the lithium-containing silicon oxide particles, a conductive auxiliary agent, and a binder to provide a slurry, and applying the slurry on a surface of a current collector and drying the slurry.
13. The negative electrode for a nonaqueous electrolyte secondary battery according to claim 1 , wherein the average value of height of the protrusions is 2% to 19% of the average particle diameter of the lithium-containing silicon oxide particles.