Titanium material for hot rolling and method of producing the same
View Patent ↗The present invention provides a titanium material for hot rolling which enables reduction of defects on the surface (in the case of a flat material or strip coil, including not only the flat surfaces but also the side surfaces and edges) due to hot rolling. The titanium material for hot rolling has dimples imparted by cold plastic deformation whose mean value of the heights (Wc) of the undulation profile elements is 0.2 to 1.5 mm and mean value of the lengths (WSm) thereof is 3 to 15 mm. The invention also provides a method of producing the titanium material and a method of hot rolling the titanium material.
1. A titanium material for hot rolling into a flat material, bar or rod, characterized in that its surface has dimples imparted by cold plastic deformation whose mean value of the heights (Wc) of the undulation profile elements is 0.2 to 1.5 mm and mean value of the lengths (WSm) thereof is 3 to 15 mm.
2. The titanium material for hot rolling of claim 1 , characterized in that the titanium material for hot rolling is a rectangular or cylindrical ingot.
3. A method of hot-rolling the titanium materials for hot rolling of claim 2 , characterized in that a slab shape produced in an electron beam melting furnace is fed into a hot rolling mill after heating and hot rolled into a strip coil.
4. The titanium material for hot rolling of claim 1 or 2 , characterized in that the titanium material for hot rolling is made of commercially pure titanium.
5. A method of producing the titanium material for hot rolling of claim 1 or 2 , characterized in that the surface of the titanium material is plastically deformed by cold pounding with a steel tool having a tip shape of a radius of curvature of 3 to 30 mm.
6. A method of producing the titanium material for hot rolling of claim 1 or 2 , characterized in that the surface of the titanium material is plastically deformed by cold pounding with a steel sphere of a radius of 3 to 30 mm.