Microcapsule corrosion control in reinforced concrete
View Patent ↗Corrosion control in reinforced concrete is generally disclosed. Some example embodiments may include concrete including aggregate, cement, and/or microcapsules distributed within the cement, where the individual microcapsules may include a high pH salt substantially contained within an acid-soluble shell. If the pH of the concrete decreases, the acid soluble shell may swell and/or dissolve, such as below a pH of about 11, which may release the high pH salt. The high pH salt may locally increase the pH of the concrete. By increasing the pH above about pH 11, corrosion of steel rebar may be prevented and/or reduced.
1. A concrete composition comprising:
an aggregate;
a cement that is mixed with the aggregate;
a plurality of microcapsules distributed within the cement, individual microcapsules comprising an acid-soluble shell, wherein the shell includes a polymer comprising imidazoline subunits and is insoluble in water above about pH 12 and is at least partially soluble in water below about pH 11; and
in response to a decrease of a pH of the concrete composition below about pH 11, the salt is releasable to increase the pH of the concrete composition to above about pH 11 to prevent a corrosion within the concrete composition.
2. The composition of claim 1 , wherein the salt comprises one or more of a phosphate, and a carbonate.
3. The composition of claim 1 , wherein the salt comprises sodium carbonate.
4. The composition of claim 1 , wherein the shell comprises an acid-soluble polymer.
5. The composition of claim 1 , wherein the imidazoline subunits have a pKa of about 10.8.
6. The composition of claim 5 , wherein the polymer comprising the imidazoline subunits comprises about 20% to about 30% imidazoline and about 70% to about 80% styrene.
7. The composition of claim 1 , wherein the microcapsules comprise about 0.1% to about 10% of the cement by volume.
8. The composition of claim 1 , wherein the microcapsules comprise about 1% to about 5% of the cement by volume.
9. The composition of claim 1 , wherein a ratio by weight of the salt to the cement is about 0.0001: 1 to about 0.0020: 1.
10. The composition of claim 1 , wherein a ratio by weight of the salt to the cement is about 0.0001:1.
11. The composition of claim 1 , wherein a ratio by weight of the salt to the cement is about 0.0005:1.
12. The composition of claim 1 , wherein a ratio by weight of the salt to the cement is about 0.0010:1.