Polyolefin composition for water pipes with good resistance to chlorine dioxide and low migration
View Patent ↗The present invention relates to a polyolefin composition with good resistance to degradation caused by chlorine dioxide-containing water and at the same time showing low migration of the used additives and its decomposition products, especially phenols, out of the composition. The present invention is also directed to a pipe made of such a polyolefin composition. The present invention further relates to the use of the polyolefin composition for the production of a pipe and to the use of a combination of particular types of antioxidants for increasing the resistance of a polyolefin composition against degradation caused by contact with chlorine dioxide-containing water and for maintaining at the same time a low migration of the used additives and its decomposition products, especially phenols, out of the polyolefin composition.
1. A pipe formed of a polyolefin composition consisting of
a) a polyolefin base resin (A) consisting of a polyethylene homo- or copolymer, and a specific combination of two antioxidants consisting of (B) and (C):
b) 150 to 500 ppm of an antioxidant (B) according to formula (I):
wherein R 1 , R 2 , R 3 , R 4 and R 5 independently are H, or non-substituted or substituted aliphatic or aromatic hydrocarbyl radicals which may comprise heteroatoms, and
c) 1600 to 5000 ppm of an antioxidant (C) according to formula (II):
wherein R 6 , R 7 and R 8 independently are non-substituted or substituted aliphatic or aromatic hydrocarbyl radicals which may comprise OH-groups, X 1 , X 2 , and X 3 independently are H or OH, with the provisio that at least one of X 1 , X 2 , and X 3 is OH, the entire molecule does not comprise an ester group, and the concentration of antioxidants (B) and (C) in the polyolefin composition is based on the total composition, and wherein a failure time of said pipe exceeds 1165 hours when tested according to ASTM F2263-03, modified by replacing chlorine with chlorine dioxide.
2. The pipe according to claim 1 , wherein the concentration of antioxidant (C) in the polyolefin composition is at least 3400 ppm, based on the total composition.
3. The pipe according to claim 1 , wherein antioxidant (C) is 1,3,5-Trimethyl-2,4,6-tris(3,5-di-tert. butyl-4-hydroxyphenyl)benzene.
4. The pipe according to claim 1 , wherein antioxidant (B) is 2,5,7,8-Tetramethyl-2-(4′,8′,12′-trimethyltridecyl)chroman-6-ol.
5. The pipe according to claim 1 , wherein from the composition an amount of at most 20 microgram of phenolic decomposition and/or by-products per liter of water (μ/L) migrates into water, measured according to the migration-into-water analysis method.
6. A pipe formed of a polyolefin composition consisting of
a) a polyolefin base resin (A) consisting of a polyethylene homo- or copolymer, and a specific combination of two antioxidants consisting of (B) and (C):
b) 150 to 500 ppm of an antioxidant (B) according to formula (I):
wherein R 1 , R 2 , R 3 , R 4 and R 5 independently are H, or non-substituted or substituted aliphatic or aromatic hydrocarbyl radicals which may comprise heteroatoms,
c) 1600 to 5000 ppm of an antioxidant (C) according to formula (II):
wherein R 6 , R 7 and R 8 independently are non-substituted or substituted aliphatic or aromatic hydrocarbyl radicals which may comprise OH-groups, X 1 , X 2 , and X 3 independently are H or OH, with the provisio that at least one of X 1 , X 2 , and X 3 is OH, the entire molecule does not comprise an ester group, and the concentration of antioxidants (B) and (C) in the polyolefin composition is based on the total composition, and wherein a failure time of said pipe exceeds 1165 hours when tested according to ASTM F2263-03, modified by replacing chlorine with chlorine dioxide, and
d) optionally pigments, stabilizers, anti-acids, anti-UV agents, antistatic agents and processing aids in an amount of 10 wt % or below.
7. A method for the transport of chlorine dioxide-containing water, comprising passing chlorine dioxide-containing water through a pipe according to claim 1 .
8. A method for increasing the resistance of a polyolefin composition against degradation caused by contact with chlorine dioxide-containing water, comprising formulating a polyolefin composition consisting of
a polyolefin base resin (A) consisting of a polyethylene homo- or copolymer with a specific combination of two antioxidants consisting of (B) and (C):
antioxidant (B) according to formula (I):
wherein R 1 , R 2 , R 3 , R 4 and R 5 independently are H, or non-substituted or substituted aliphatic or aromatic hydrocarbyl radicals which may comprise heteroatoms, and
antioxidant (C) according to formula (II):
wherein R 6 , R 7 and R 8 independently are non-substituted or substituted aliphatic or aromatic hydrocarbyl radicals which may comprise OH-groups, X 1 , X 2 , and X 3 independently are H or OH, with the provisio that at least one of X 1 , X 2 , and X 3 is OH, the entire molecule does not comprise an ester group, and the concentration of antioxidant (B) is from 150 to 500 ppm, and the concentration of antioxidant (C) in the polyolefin composition is from 1600 to 5000 ppm, based on the total composition, such that a failure time of said pipe exceeds 1165 hours when tested according to ASTM F2263-03, modified by replacing chlorine with chlorine dioxide.