Polyamide resin composition reinforced with glass fiber
There is provided a polyamide resin composition reinforced with glass fiber produced by the melt kneading of a mixture where 60 to 80 parts by weight of glass fiber bundles (B) comprising a glass fiber having a flat cross section whose flatness degree is 1.5 to 8 and having an ignition loss at 625° C. for 0.5 hour of not more than 0.8% by weight are added to 40 to 20 parts by weight of polyamide (A), characterized in that, during the above melt kneading, a polyamide-reactive silane coupling agent (C) is added to the above mixture in a rate of 0.1 to 1.0% by weight of the above glass fiber bundles (B). The polyamide resin composition of the present invention has high bending strength, bending elastic modulus and Charpy impact strength (at 23° C. and −40° C.) by a specific fracture mode which have been never achieved before, and it is excellent in productivity.
1. A polyamide resin composition reinforced with glass fiber produced by the melt kneading of a mixture where 66 to 80 parts by weight of glass fiber bundles (B) comprising a glass fiber having a flat cross section whose flatness degree is 1.5 to 8 and having an ignition loss at 625° C. for 0.5 hour of not more than 0.8% by weight are added to 34 to 20 parts by weight of polyamide (A), characterized in that, during the above melt kneading, a polyamide-reactive silane coupling agent (C) is added to the above mixture in a rate of 0.1 to 1.0% by weight of the above glass fiber bundles (B),
wherein the polyamide resin (A) is constituted from an aliphatic polyamide (a1) and a polyamide (a2) containing aromatic components, and their constituting ratio by weight is (5 to 95):(95 to 5), and
wherein the polyamide resin composition does not contain a flame retardant.
2. The polyamide resin composition reinforced with glass fiber according to claim 1 , wherein the polyamide (a2) containing the aromatic components contains poly-m-xylylene adipamide which has a relative viscosity in a 96% sulfuric acid solution of 1.4 to 1.8 and has a terminal carboxyl group concentration of not higher than 50 meq/kg.
3. The polyamide resin composition reinforced with glass fiber according to claim 1 , wherein the aliphatic polyamide (a1) contains polycaproamide which has a relative viscosity in a 96% sulfuric acid solution of 1.4 to 2.0 and has a terminal carboxyl group concentration of 55 to 95 meq/kg.
4. The polyamide resin composition reinforced with glass fiber according to claim 1 , wherein the bending elastic modulus (in accordance with ISO 178) is not less than 23 GPa.
5. The polyamide resin composition reinforced with glass fiber according to claim 1 , wherein, in the fractured surface of the test piece of the polyamide resin composition reinforced with glass fiber after the Charpy impact strength test (in accordance with ISO 179-1; cutting notch portion), the area ratio of the apparent surface area (SA) of the fractured surface to the cross sectional area (SB) of the notch portion is not less than 2.5;
the apparent surface area (SA) of the fractured surface: area which is calculated by (fracture length from the front end of the notch portion to the opposite side surface of the notch portion)×(thickness of the test piece); and
the cross sectional area (SB) of the notch portion: area which is calculated by (width of the notch portion)×(thickness of the test piece).
6. The polyamide resin composition reinforced with glass fiber according to claim 2 , wherein the aliphatic polyamide (a1) contains polycaproamide which has a relative viscosity in a 96% sulfuric acid solution of 1.4 to 2.0 and has a terminal carboxyl group concentration of 55 to 95 meq/kg.
7. The polyamide resin composition reinforced with glass fiber according to claim 2 , wherein the bending elastic modulus (in accordance with ISO 178) is not less than 23 GPa.
8. The polyamide resin composition reinforced with glass fiber according to claim 3 , wherein the bending elastic modulus (in accordance with ISO 178) is not less than 23 GPa.
9. The polyamide resin composition reinforced with glass fiber according to claim 2 , wherein, in the fractured surface of the test piece of the polyamide resin composition reinforced with glass fiber after the Charpy impact strength test (in accordance with ISO 179-1; cutting notch portion), the area ratio of the apparent surface area (SA) of the fractured surface to the cross sectional area (SB) of the notch portion is not less than 2.5;
the apparent surface area (SA) of the fractured surface: area which is calculated by (fracture length from the front end of the notch portion to the opposite side surface of the notch portion)×(thickness of the test piece); and
the cross sectional area (SB) of the notch portion: area which is calculated by (width of the notch portion)×(thickness of the test piece).
10. The polyamide resin composition reinforced with glass fiber according to claim 3 , wherein, in the fractured surface of the test piece of the polyamide resin composition reinforced with glass fiber after the Charpy impact strength test (in accordance with ISO 179-1; cutting notch portion), the area ratio of the apparent surface area (SA) of the fractured surface to the cross sectional area (SB) of the notch portion is not less than 2.5;
the apparent surface area (SA) of the fractured surface: area which is calculated by (fracture length from the front end of the notch portion to the opposite side surface of the notch portion)×(thickness of the test piece); and
the cross sectional area (SB) of the notch portion: area which is calculated by (width of the notch portion)×(thickness of the test piece).
11. The polyamide resin composition reinforced with glass fiber according to claim 1 , wherein the composition has a bending strength of not less than 400 MPa.