Hydroxyapatite poly(etheretherketone) nanocomposites and method of manufacturing same
View Patent ↗Hydroxyapatite-polymer nanocomposites, which are nanoparticles/microparticles, methods for making them, and articles made from them are disclosed. These methods are capable of preparing nanocomposites exhibiting more homogeneous dispersion of nanoparticles than is seen using previous methods. Such nanocomposites and articles are useful for a wide variety of applications, such as biological, medical, biochemical, biosensor, fuel cell, and aerospace applications.
1. A method comprising:
precipitating a calcium apatite particle from a solution onto a surface of a polymer particle to form a composite particle,
forming a pellet comprising at least two of the composite particles; and
sintering the pellet in at least a first and a second stage to form a sintered pellet; wherein:
the solution comprises water, calcium oxide, and phosphoric acid;
the first stage is performed at a temperature below a melting temperature of the polymer particle; and
the second stage is performed at a temperature above the melting temperature of the polymer particle.
2. The method of claim 1 , wherein the polymer particle is between 200 nm and 2 microns in diameter.
3. The method of claim 1 , wherein the polymer particle comprises polyetheretherketone and the calcium apatite particle comprises hydroxyapatite, which is nanocrystalline and size of 5 nm to 100 nm.
4. The method of claim 1 , wherein the forming comprises milling the composite particle.
5. The method of claim 1 , wherein the composite particle is a nanocomposite particle.
6. The method of claim 1 , wherein the composite particle comprises a ratio of calcium to phosphorous atoms between 1.5 and 1.8.
7. The method of claim 1 , wherein the composite particle comprises at least 40 wt % of the polymer and less than 60 wt % of the calcium apatite.
8. The method of claim 1 , wherein the pellet includes a shell surrounding a core, wherein the shell includes the calcium apatite and the core comprises the polymer.
9. The method of claim 1 , wherein the sintering comprises liquid sintering.
10. The method of claim 1 , wherein the sintered pellet comprises at least 50 wt % of the polymer and less than 50 wt % of the calcium apatite.
11. The method of claim 1 , wherein the polymer particle comprises polyetheretherketone.
12. The method of claim 1 , wherein the polymer comprises polyetheretherketone, the first stage is performed at about 320° C. and the second stage is performed at a temperature of about 345° C.
13. The method of claim 1 further comprising sintering in a third stage at a temperature of about 370° C.