Porous electrode substrate, method for producing the same, membrane electrode assembly, and polymer electrolyte fuel cell
View Patent ↗Provided is a porous electrode substrate having high mechanical strength, good handling properties, high thickness precision, little undulation, and adequate gas permeability and conductivity. Also provided is a method for producing a porous electrode substrate at low costs. A porous electrode substrate is produced by joining short carbon fibers (A) via mesh-like of carbon fibers (B) having an average diameter of 4 μm or smaller. Further provided are a membrane-electrode assembly and a polymer electrolyte fuel cell that use this porous electrode membrane. A porous electrode substrate is obtained by subjecting a precursor sheet, in which short carbon fibers (A) and short carbon fiber precursors (b) having an average diameter of 5 μm or smaller have been dispersed, to carbonization treatment after optional hot press forming and optional oxidization treatment.
1. A method for producing a porous electrode substrate, comprising:
producing a precursor sheet comprising short carbon fibers (A) and short carbon fiber precursors (b) dispersed therein, wherein the short carbon fiber precursors (b) have an average diameter of 5 μm or smaller and a length of from 2 to 20 mm, and the short carbon fiber precursors (b) are obtained by cutting long carbon fiber precursors; and
then subjecting the precursor sheet to carbonization treatment at a temperature of 1,000° C. or higher to obtain a porous electrode substrate in which the short carbon fibers (A) are joined via mesh carbon fibers (B) having an average diameter of 4 μm or smaller,
wherein the mesh carbon fibers (B) are obtained by contacting the short carbon fiber precursors (b) with the short carbon fibers (A).
2. The method according to claim 1 , further comprising subjecting the precursor sheet to hot press forming at a temperature of lower than 200° C. between the producing and the subjecting to carbonization treatment.
3. The method according to claim 2 , further comprising subjecting the precursor sheet, which has been subjected to the hot press forming, to oxidization treatment at a temperature between 200° C. to less than 300° C., between the hot press forming and the subjecting to carbonization treatment.
4. The method according to claim 1 , wherein the short carbon fiber precursors (b) have an average diameter of from 3 μm to 5 μm.
5. The method according to claim 1 , wherein the short carbon fiber precursors (b) have an average diameter of from 4 μm to 5 μm.
6. The method according to claim 1 , wherein the short carbon fiber precursors (b) are selected from a polyacrylonitrile-based short carbon fiber precursor, a cellulose-based short carbon fiber precursor, and a phenol-based short carbon fiber precursor.
7. The method according to claim 1 , wherein an amount of the short carbon fiber precursors (b), based on 100 parts by mass of the short carbon fibers (A) is from 50 to 300 parts by mass.