Thermoplastic molding compounds based on styrene copolymers and polyamides having improved weathering resistance

1. A thermoplastic molding composition, consisting of

a) as component A, from 3 to 78% by weight of one or more styrene copolymers which have no units derived from maleic anhydride,

b) as component B, from 15 to 90% by weight of one or more polyamides,

c) as component C, from 5 to 50% by weight of one or more impact-modifying graft rubbers without olefinic double bonds in the rubber phase, whereby the graft rubbers are core-shell rubbers composed of at least one hard and one soft constituent, whereby the soft constituent derives from butylacrylate and the hard constituent derives from styrene, 2-methylstyrene and copolymers comprising styrene 2-methylstyrene, or acrylonitrile,

d) as component D, from 1 to 25% by weight of one or more styrene copolymers which have, based on the entire component D, from 0.5 to 5% by weight of units derived from maleic anhydride,

e) as component E, from 1 to 30% by weight of one or more further rubbers based on olefinic monomers without core-shell structure, and having at least 0.1% by weight of functional monomers,

f) as component F, from 0 to 50% by weight of one or more fibrous or particulate fillers,

g) as component G, from 17 to 40% by weight of further additives, wherein component G is selected from the group consisting of flame retardants, dyes, pigments, stabilizers, demolding aids, and combinations thereof;

where the entire amount of components A to G does not exceed 100% by weight;

wherein component E is a copolymer comprising

e1) from 35 to 89.95% by weight of ethylene, as component E1,

e2) from 10 to 60% by weight of 1-octene, 1-butene, propene, or a mixture thereof, as component E2, and

e3) from 0.05 to 5% by weight of functional monomers, where the monomers bear functional groups selected from the group consisting of carboxylic acid groups, carboxylic anhydride groups, carboxylic ester groups, carboxamide groups, carboximide groups, amino groups, hydroxy groups, epoxide groups, urethane groups, oxazoline groups, and mixtures thereof.

2. The molding composition according to claim 1 , wherein component D has from 1.0 to 2.5% by weight of units derived from maleic anhydride.

3. The molding composition according to claim 2 , wherein component D has from 1.7 to 2.3% by weight of units derived from maleic anhydride.

4. The molding composition according to claim 1 , wherein the molding composition comprises less than 0.1% by weight of phthalic anhydride.

5. The molding composition according to claim 1 , wherein component B has from 0.05 to 0.5% by weight of triacetonediamine (TAD) end groups.

6. The molding composition according to claim 1 , wherein component D is a styrene-acrylonitrile-maleic anhydride (MSA) terpolymer or styrene-N-phenylmaleinimide-maleic anhydride terpolymer.

7. The molding composition according to claim 1 , wherein component A is a styrene-acrylonitrile copolymer.

8. The molding composition according to claim 1 , wherein component C is an acrylate-styrene-acrylonitrile (ASA) graft rubber.

9. A process for the production of thermoplastic molding compositions according to claim 1 , which comprises mixing components A to E and G, and optionally F with one another, wherein component E is first premixed with at least one portion of component B to give a masterbatch, which is then mixed with the further components of the thermoplastic molding composition.

10. A molding, fiber, or foil comprising the thermoplastic molding composition according to claim 1 .

11. The molding, fiber, or foil of claim 10 , wherein the molding is a motor-vehicle component or part of electronic equipment.