Sulfonated block copolymer fluid composition for preparing membranes and membrane structures
View Patent ↗The present invention relates to an improved method for making sulfonated block copolymers and to methods for making membranes from such block copolymers. In particular, the present invention relates to an improved method for making sulfonated block copolymers having at least two polymer end blocks that are resistant to sulfonation and at least one polymer interior block that is susceptible to sulfonation where the sulfonation agent is C 2 to C 8 acyl sulfate. In the improved process the residual carboxylic acid formed from the C 2 to C 8 acyl sulfate is converted to C 1 to C 4 alkyl esters by contacting the residual carboxylic acid with at least a 0.9:1 molar ratio of a C 1 to C 4 alcohol to residual carboxylic acid, resulting in an improved sulfonated block copolymer solution. The present invention further relates to the use of such sulfonated block copolymer solutions to prepare various membranes and other articles.
1. A fluid composition comprising the sulfonated block copolymer, ester of residual carboxylic acid and at least one non-halogenated aliphatic solvent prepared by the steps of:
(a) providing a precursor block copolymer having at least two end blocks A and at least one interior block B, wherein each A block is a polymer block resistant to sulfonation and each B block is a polymer block susceptible to sulfonation;
(b) reacting the precursor block polymer with a C2 to C8 acyl sulfate in a reaction mixture further comprising at least one non-halogenated aliphatic solvent to form a sulfonated block polymer, therein resulting in the formation of a solution of a sulfonated block copolymer and a residual carboxylic acid; and
(c) subsequently reacting the residual carboxylic acid contacted with a C1 to C4 alcohol or mixture thereof in a molar ratio of alcohol to residual carboxylic acid of at least 0.9:1 to form the corresponding alkyl esters of the carboxylic acid and to reduce the residual level of the organic residual acid to less than 2.0 wt % based on the total weight of the solution,
wherein the reaction mixture is free of any halogenated solvent, and wherein the concentration of sulfonated block copolymer is 2 wt % to 30 wt %, based on the total weight of the fluid composition.
2. The fluid composition of claim 1 wherein the concentration of sulfonated block copolymer is 5 to 20 wt %.
3. The fluid composition of claim 1 wherein said sulfonated block copolymer prior to hydrogenation has the general configuration (A-D-B) n X, wherein n is an integer from 2 to about 30, and X is a coupling agent residue and wherein said A block is a polymer block of para-t-butylstyrene, said B block is a polymer block of unsubstituted styrene and said D block is a polymer block of isoprene or 1,3-butadiene wherein 20 to 80 mol percent of the condensed butadiene units in block D have 1,2-configuration, said ester of residual carboxylic acid is the methyl or ethyl ester of isobutyric acid and said non-halogenated aliphatic solvent has a boiling point range of between 70 and 220° C.