Catalytic production processes for making tetrafluoropropenes and pentafluoropropenes
View Patent ↗A process is disclosed for making CF 3 CF═CHF. The process involves contacting at least one hexafluoropropane selected from the group consisting of CF 3 CF 2 CH 2 F and CF 3 CHFCHF 2 with a chromium oxyfluoride catalyst in a reactor to obtain a product mixture comprising CF 3 CF═CHF, and recovering CF 3 CF═CHF from the product mixture. A process is disclosed for making CF 3 CH═CHF. The process involves contacting CF 3 CH 2 CHF 2 with a chromium oxyfluoride catalyst in a reactor to obtain a product mixture comprising CF 3 CH═CHF, and recovering CF 3 CH═CHF from the product mixture. A process is disclosed for making CF 3 CF═CH 2 . The process involves contacting CF 3 CF 2 CH 3 with a chromium oxyfluoride catalyst in a reactor to obtain a product mixture comprising CF 3 CF═CH 2 , and recovering CF 3 CF═CH 2 from the product mixture.
1. A process comprising: (a) contacting 1,1,1,2,2-pentafluoropropane with a chromium oxyfluoride catalyst in a reactor to obtain a product mixture comprising 2,3,3,3-tetrafluoropropene; and (b) recovering said 2,3,3,3-tetrafluoropropene from said product mixture; wherein said chromium oxyfluoride catalyst is represented by formula Cr 2 O x F y wherein x+y/2=3.
2. The process of claim 1 wherein said catalyst has surface areas of about 20 m 2 /g to about 500 m 2 /g.
3. The process of claim 1 wherein said catalyst has surface areas of about 40 m 2 /g to about 350 m 2 /g.
4. The process of claim 1 wherein said catalyst has surface areas of about 60 m 2 /g to about 300 m 2 /g.
5. The process of claim 1 wherein said catalyst has surface areas of about 100 m 2 /g to about 300 m 2 /g.
6. The process of claim 1 wherein said catalyst contains an alkali metal content of about 2000 ppm or less.
7. The process of claim 1 wherein said catalyst contains an alkali metal content of about 300 ppm or less.
8. The process of claim 1 wherein said catalyst contains an alkali metal content of about 100 ppm or less.
9. The process of claim 1 wherein said contact is conducted at a temperature of from about 200° C. to about 500° C.
10. The process of claim 1 wherein said contact is conducted at a temperature of from about 300° C. to about 400° C.
11. The process of claim 1 wherein said catalyst is amorphous.
12. The process of claim 1 wherein said catalyst is prepared from crystalline α-Cr 2 O 3 .
13. The process of claim 1 wherein said catalyst is produced in situ.
14. The process of claim 1 wherein an inert gas is also fed to said reactor.
15. The process of claim 14 wherein said inert gas is nitrogen.
16. The process of claim 1 wherein a gas comprising oxygen is also fed to said reactor.
17. The process of claim 16 wherein said gas is air.