Heavy metal removal methods and systems
View Patent ↗A support impregnated with selenium and capable of effectively removing a heavy metal from a process stream that is at an ambient temperature or is at an elevated temperature.
1. A system comprising:
a porous activated carbon support impregnated with powdered elemental selenium at a temperature of 650 degrees Celsius in a vacuum chamber, wherein the porous activated carbon support is made of a substrate made porous; and
a liquid process stream at about 100 degrees Celsius in fluid communication with the support, wherein the process stream contains mercury for removal using the porous activated carbon support.
2. The system of claim 1 , wherein the impregnated support has 6.5 wt. % or greater selenium.
3. The system of claim 1 , wherein the porous support is shaped into particles or pellets about 10 mm in length or less.
4. A support comprising:
an activated carbon substrate impregnated in a vacuum with powdered elemental selenium at 650 degrees Celsius to provide the support that is at a temperature greater than 100° C. and is suitable for use in removal of mercury from a liquid process stream, wherein the substrate is activated to become porous before being impregnated.
5. The support of claim 4 , wherein the impregnated substrate has 6.5 wt. % or greater selenium.
6. A method comprising:
preparing a porous support, wherein a substrate for the porous support is activated to become porous;
impregnating the porous support with powdered selenium at 650 degrees Celsius in a vacuum environment to create an impregnated porous support;
preparing a bed of the impregnated porous support;
running a liquid process stream through the bed with the temperature of the porous support at about 100 degrees Celsius;
removing mercury from the liquid process stream by sorbing mercury on the porous support, which is at a temperature of about 100 degrees Celsius;
removing the porous support from the liquid process stream;
regenerating the porous support by heating the porous support to above 150 degrees Celsius thereby desorbing the mercury from the porous support.
7. The method of claim 6 , wherein the step of impregnating the porous support occurs for at least about 120 minutes.
8. The method of claim 6 , wherein the step of impregnating the porous support includes placing the porous support with powdered selenium in an inert environment.