View Patent ↗Articles, such as tubing or strips, which have excellent corrosion resistance to water or steam at elevated temperatures, are produced from alloys having 0.2 to 1.5 weight percent niobium, 0.01 to 0.6 weight percent iron, and optionally additional alloy elements selected from the group consisting of tin, chromium, copper, vanadium, and nickel with the balance at least 97 weight percent zirconium, including impurities, where a necessary final heat treatment includes one of i) a SRA or PRXA (15-20% RXA) final heat treatment, or ii) a PRXA (80-95% RXA) or RXA final heat treatment.
1. A method of making a zirconium based alloy article which exhibits one of improved corrosion resistance and improved creep resistance for use in an elevated temperature environment of a nuclear reactor, comprising the steps:
(a) combining
0.4 to 1.5 weight percent niobium,
0.4 to 0.8 weight percent tin,
0.05 to 0.3 weight percent iron,
0.0 to 0.5 weight percent chromium, and
the balance at least 97 weight percent zirconium including impurities to provide an alloy mixture;
(b) melting the alloy mixture to produce a melted alloy material;
(c) forging the melted alloy material to produce a forged alloy material;
(d) quenching the forged alloy material to produce a quenched alloy material;
(e) rolling the quenched alloy material to produce a rolled alloy material;
(f) annealing the rolled alloy material to produce an annealed alloy material;
(g) following completion of steps (b), (c), (d), (e) and (f), subjecting the annealed alloy material to a final heat treatment selected to provide a zirconium-based alloy exhibiting one of improved corrosion resistance and improved creep resistance,
wherein for providing the zirconium-based alloy exhibiting improved corrosion resistance, the annealed alloy material is subjected to a final heat treatment of partial recrystallization to produce an amount of recrystallization from about 15% to 20% with the remainder being stress relief annealed, and
wherein for providing the zirconium-based alloy exhibiting improved creep resistance, the annealed alloy material is subjected to a final heat treatment of partial recrystallization to produce an amount of recrystallization from about 80% to 95% recrystallization with the remainder being stress relief annealed.
2. The method of making the zirconium based alloy of claim 1 , wherein the alloy has a composition of about:
0.4 to 1.5 weight percent niobium,
0.6 to 0.7 weight percent tin,
0.05 to 0.3 weight percent iron,
the balance at least 97 weight percent zirconium, including impurities.
3. The method of making the zirconium based alloy of claim 1 , wherein the alloy has a composition of about:
0.4 to 1.5 weight percent niobium,
0.61 to 0.69 weight percent tin,
0.05 to 0.3 weight percent iron,
the balance at least 97 weight percent zirconium, including impurities.
4. The method of making the zirconium alloy of claim 1 , wherein the alloy further comprises:
0.05 to 0.5 weight percent chromium.